Sikaflex® PRO-3 Purform®

• Contributes towards satisfying Indoor Environmental Quality (EQ) Credit: Low-Emitting Materials under LEED® v4.

• VOC emission classification GEV Emicode EC1^plus.

• CE marking and declaration of performance based on EN 15651-1:2012 Sealants for non-structural use in joints in buildings and pedestrian walkways — Part 1: Sealants for facade elements.

• CE marking and declaration of performance based on EN 14188-2:2004 Joint fillers and sealants — Part 2: Specifications for cold applied sealants.

• CE marking and declaration of performance based on EN 15651-4:2012 Sealants for non-structural use in joints in buildings and pedestrian walkways — Part 4: Sealants for pedestrian walkways.

• Tensile Properties, Adhesion, Change of Volume tests ISO 11600 F Class 25 HM.

• Standard Specification for Elastomeric Joint Sealants, ASTM C 920.

• Chemical Resistance, DIN EN 14187, SKZ, Report No. 208323/20.

• Determination of the staining, ASTM 1248-04, SKZ, Report No.205279/19-VI.

• Waste water, DIBt, SKZ, Test Report No. 205279/19-V.

• Outgassing VOC/SVOC, CSM procedures, Fraunhofer, Certificate, No. SI 1909-1140.

• Testing of joint sealant for pedestrian walkways ISO 11618, SKZ, No. 205279/19-VII.

• Sealants - Durability to extension compression, ISO 19862, Sikaflex® PRO-3 Purform.

Sika® Purform® Polyurethane Technology

15 months from date of production

The Product must be stored in original, unopened and undamaged sealed packaging in dry conditions at temperatures between +5 °C and +25 °C. Always refer to the packaging.

Refer to the current Safety Data Sheet for information on safe handling and storage.

• Non-staining on many natural stones according to ASTM 1248-04 / ISO 16938-1.

• To confirm suitability, tests must be carried out according to ISO 16938-1/ ASTM 1248-04 before using on natural stones and full project application.

40 (after 28 days)

Resistant to many chemicals. Refer to the following test report or contact Sika Technical Services for additional information:

Chemical Resistance, DIN EN 14187, SKZ, Report No. 208323/20.

For movement joints, the width must be at least 8 mm and should not exceed 40 mm. For non-movement joints such as connection joints in interior areas, the joint width can be less than 8 mm.

The joint dimensions must be designed to suit the movement capability of the sealant. In all cases joints must be at least 8 mm deep, or a have a width to depth ratio of 1 : 0.5 for the facade joints or 1 : 0.8 for floor joints whichever is greater.

For more information about joint design and calculations refer to the Sika document Design guideline: Dimensioning of construction joints or contact Sika Technical Services.

For applications at temperatures below +5 °C, please contact Sika Techincal Services.

The substrate temperature must be +3 °C above dew point temperature and free from frost and ice.

Use closed cell, polyethylene foam backing rod.

3.5 mm/24 hours (+23 °C / 50 % r.h.)

50 minutes (+23 °C / 50 % r.h.)

40 minutes (+23 °C / 50 % r.h.)

IMPORTANT

Poor adhesion due to inadequate surface preparation

Primers are adhesion promoters.

1. Do not use primers for improving poorly prepared or poorly cleaned joint surfaces.

IMPORTANT

Poor adhesion due to incorrect priming procedure

Incorrectly defined or uncontrolled priming procedures may lead to a variation in Product performance.

1. Test adhesion on project-specific substrates and agree on procedures with all parties before full project application. For more information contact Sika Technical Services.

The substrate must be sound, clean, dry and free of contaminants such as dirt, oil, grease, cement laitance, sealant residues and poorly bonded coatings which could affect adhesion of the primer and sealant.

The substrate must be of sufficient strength to cope with the stresses induced by the sealant during movement.

1. Use techniques such as wire brushing, grinding, grit blasting or other suitable mechanical methods to remove all weak substrate material.
2. Repair all damaged joint edges with suitable Sika repair products.
3. Remove dust, loose and friable material from all surfaces before applying the sealant.

If tested or supported by experience, the Product can be used without primers or activators on many substrates.

Use the following priming or pre-treatment procedures to ensure optimum adhesion and joint durability, or if the Product is used for high-performance applications such as joints on multi-storey buildings, highly stressed joints, or joints exposed to extreme weather.

NON-POROUS SUBSTRATES

Aluminium, anodised aluminium, stainless steel, galvanised steel or glazed tiles:

1. Lightly roughen the surface with a fine abrasive pad.
2. Clean the surface.
3. Pretreat the surface with Sika® Aktivator-205 applied with a clean cloth.

Other metals, such as copper, brass and titanium-zinc:

1. Lightly roughen the surface with a fine abrasive pad.
2. Clean the surface.
3. Pretreat the surface with Sika® Aktivator-205 applied with a clean cloth.
4. Wait until the flash-off time is over.
5. Prime the surface with Sika® Primer-3 N applied with a brush.

Powder-coated metals:

1. Carry out preliminary trials to verify adhesion. For more information contact Sika Technical Services.

PVC substrates:

1. Prime the surface with Sika® Primer-215 applied with a brush.  

POROUS SUBSTRATES

Concrete, aerated concrete and cement based renders, mortars and bricks:

1. Prime the surface with Sika® Primer-3 N or Sika® Primer-115 applied with a brush.

Concrete that is 2 to 3 days old, or matt wet (surface dry):

1. Prime the surface with Sika® Primer-115 applied with a brush.

Reconstituted, cast stone or natural stone:

1. Carry out preliminary trials to check if the stone is susceptible to plasticiser migration. For information about a suitable primer to prevent plasticiser migration, contact Sika Technical Services.

ASPHALT (ACCORDING TO EN 13108-1 AND EN 13108-6):

Fresh cut or existing cut asphalt must have a clean bonding surface with more than 50 % exposed aggregate.

1. Prime the surface with Sika® Primer-3 N or Sika® Primer-115 applied with a brush.

For more details of the primer or pretreatment products, refer to the corresponding Product Data Sheet. Contact Sika Technical Services for additional information.

1-part ready to use.

IMPORTANT

Strictly follow installation procedures

Strictly follow installation procedures as defined in Method Statements, application manuals and working instructions which must always be adjusted to the actual site conditions.

IMPORTANT

Staining on natural stone substrates due to plasticiser migration

Staining from plasticiser migration may occur when used on cast, reconstituted or natural stone such as granite, marble or limestone substrates.  Customers should test a sample prior to application.

IMPORTANT

Degradation of sealant due to chemical attack

Do not use the Product to seal joints in and around swimming pools containing water treatment agents such as chlorine.

Do not use on bituminous substrates, natural rubber, EPDM rubber or on any building materials which might leach oils, plasticisers or solvents that could degrade the sealant.

IMPORTANT

Insufficient curing due to exposure to alcohol

Exposure to alcohol during curing may interfere with the curing reaction and cause the Product to remain soft or become tacky. 

Do not expose the Product to alcohol-containing products during the curing period.

1. Apply masking tape where neat or exact joint lines are required.
2. After the required substrate preparation, insert a backing rod to the required depth.

3. Prime the joint surfaces as recommended in substrate preparation.

   Note: Avoid excessive application of the primer.
4. Open the seal on the top of the cartridge or open the end of the foil pack.
5. Fit the nozzle and cut it to the desired bead size.
6. Insert the Product into the application gun.

7. Apply the Product into the joint.

   Note: Avoid air entrapment. Make sure that the Product comes into full contact with the adhesion area of the joint.
8. IMPORTANT Do not use tooling products containing solvents. As soon as possible after application, tool the Product firmly against the joint sides to ensure adequate adhesion and a smooth finish. Use a compatible tooling agent such as Sika® Tooling Agent N to smooth the joint surface.
9. Remove the masking tape within the skin formation time of the Product.

OVERPAINTING THE SEALANT

Sikaflex® PRO-3 can be over-painted with most conventional facade paint coating systems. However, paints must first be tested to ensure compatibility by carrying out preliminary trials (e.g. according to ISO technical paper: Paintability and Paint Compatibility of Sealants). Optimum results are obtained when the sealant is allowed to fully cure first.

IMPORTANT

Tacky paint due to plasticiser migration

Paints and sealants or adhesives may contain plasticizers and other substances that migrate and can cause the painted surface to become tacky.

IMPORTANT

Cracking paint due to joint movement

Rigid paint applied on top of a sealant or flexible adhesive may crack when used on joints subject to movement.

The Product can be overpainted with most conventional paint coating systems.

1. Allow the Product to fully cure before overpainting.
2. Before overpainting, carry out preliminary trials to test compatibility of the paint or coating system with the Product in accordance with ISO/TR 20436:2017 – Buildings and civil engineering works — Sealants — Paintability and paint compatibility of sealants.

Colour variation

Note: Colour variation may occur especially with white or other light colour shades. This effect is purely aesthetic and does not adversely influence the technical performance or durability of the Product.