Sika® Injection-101 RC
Sika® Injection-101 RC is a 2-part, polyurethane, low viscous, fast foaming, water-reactive injection resin. It cures to a dense flexible foam.
- Foaming reaction only takes place in direct contact with water
- Can be injected as a single component system
- Free foaming expansion up to 40 times
- Can be accelerated using Sika® Injection-AC10 in cold temperatures (< + 10 °C)
Usage
- Temporary waterstopping of high water intrusions in cracks, joints and cavities in concrete and masonry.
- Waterstopping in special applications such as bored or sheet pile walls, anchor heads and microtunneling.
- To achieve permanent watertight crack sealing inject with Sika® Injection-201 CE or Sika® Injection-203 after temporary waterstopping.
Advantages
- Foaming reaction only takes place in direct contact with water
- Can be injected as a single component system
- Free foaming expansion up to 40 times
- Can be accelerated using Sika® Injection-AC10 in cold temperatures (< + 10 °C)
Packaging
| Part A (Resin) | 10 or 20 kg |
| Part B ( Hardener) | 12,5 or 25 kg |
Refer to current price list for packaging variations.
Colour
| Part A (Resin) | Colourless |
| Part B (Hardener) | Brown |
Product Details
ENVIRONMENTAL INFORMATION
- FEICA Environmental Product Declaration (EPD)
APPROVALS / STANDARDS
-
Compilation of certified polyurethanes and injection processes for use on structures and components of federal traffic routes ZTV-ING, Part 3, Section 5 (RISS), Sika® Injection-101 RC, Bundesanstalt für Strassenwesen, 20.01.2016
-
Large-surface sealants suitability according to KTW recommendations, Sika® Injection-101 RC, LADR Zentrallabor, July 2019
Chemical Base
Water reactive polyurethane resin
Shelf Life
24 months from date of production
Storage Conditions
The product must be stored in original, unopened and undamaged packaging in dry conditions at temperatures between +5 °C and +35 °C. Always refer to packaging.
Density
| Part A (Resin) | ~1,0 kg/l |
| Part B (Hardener) | ~1,25 kg/l |
Values at +20 °C
Viscosity
| Part A (Resin) | ~140 mPa∙s |
| Part B (Hardener) | ~155 mPa∙s |
Values at +20 °C
Expansion
| Expansion start | ~15 seconds after contact with water |
| Expansion end | ~67 seconds |
Values at +20 °C
Application
Mixing Ratio
Part A : Part B = 1:1 by volume
Reaction times
(PM 10081-11)
| 0 % Sika® Injection-AC10 * | ||
| Material temperature | Expansion start | Expansion end |
| +5 °C | ~19 sec | ~89 sec |
| +10 °C | ~17 sec | ~88 sec |
| +20 °C | ~16 sec | ~70 sec |
| 5 % Sika® Injection-AC10 * | ||
| Material temperature | Expansion start | Expansion end |
| +5 °C | ~12 s | ~57 s |
| +10 °C | ~11 s | ~49 s |
| +20 °C | ~10 s | ~39 s |
| 10 % Sika® Injection-AC10 * | ||
| Material temperature | Expansion start | Expansion end |
| +5 °C | ~9 s | ~41 s |
| +10 °C | ~8 s | ~37 s |
| +20 °C | ~7 s | ~35 s |
* Dosage of Sika® Injection-AC10 in % by weight of Sika® Injection-101 RC (Parts A+B)
The data above are laboratory parameters and may deviate depending on the situation and conditions on site.
The reaction speed (foam formation) is influenced by the temperatures of the mixed material, the structure and the contact water, plus the hydrodynamic conditions.
Smaller volumes can be used at a ratio of Part A : Part B = 1:1 by volume
Ambient Air Temperature
+5 °C min. / +35 °C max.
Substrate Temperature
+5 °C min. / +35 °C max.
Pot Life
| ~2 hours (at + 20 °C) | (ISO 9514) |
MIXING
Empty Parts A +B into a mixing vessel and mix slowly and thoroughly for at least 3 min (max. 250 rpm) until completely mixed.
After mixing, pour the material into the pump’s feed container, stir briefly and use within the pot life.
If the substrate and/or ambient temperatures are < +10 °C, Sika® Injection-AC10 can be added to Sika® Injection-101 RC to accelerate the start of expansion.
CLEANING OF TOOLS
Clean all tools and application equipment using the
Sika®Injection Cleaning System or with Thinner C to remove
any polyurethane
residue immediately after use. Do not leave Thinner C
in the injection pump.