Sikadur®-33
Thixotropic two-part structural adhesive based on epoxy resin in a cartridge.
- Can be used on damp concrete.
- Excellent adhesion to the substrate.
- Non-sag, also overhead.
- High load capacity.
- Shrinkage-free hardening.
- Styrene-free.
Usage
As a Structural Adhesive for:- Concrete elements.
- Hard natural stone.
- Ceramics, fibre cement.
- Mortar, bricks, blocks, masonry, render, etc.
- Steel, iron, aluminium.
- Wood.
- Polyester, epoxy.
- Corners and edges.
- Holes and void filling.
- Joint arrises.
- Crack filling and sealing (non-moving).
- Fixing and fastening of handrails, railings, balustrades and supports.
- Fixing of window and door frames.
- Concrete.
- Hard natural stone.
- Solid rock.
- Hollow and solid masonry.
- Steel.
- Wood.
Advantages
- Can be used on damp concrete.
- Excellent adhesion to the substrate.
- Non-sag, also overhead.
- High load capacity.
- Shrinkage-free hardening.
- Styrene-free.
Packaging
250 ml cartridge, 12 per box
Pallet: 60 boxes with 12 cartridges
Colour
Part A: white
Part B: grey
Part A+B mixed: grey
Product Details
APPROVALS / STANDARDS
Tested in accordance with EN 1504-4.
Chemical Base
Epoxy resin.
Shelf Life
12 months from date of production if stored properly in undamaged and unopened. On each Sikadur®-33 cartridge the best before date is printed.
Storage Conditions
Cool and dry conditions, at temperatures between +10°C and +30°C. Protect from direct sunlight.
Density
1.35 kg/l (part A+B mixed)
Compressive Strength
~50 N/mm2 (14 days, +23°C) | (According to EN 12190) |
Flexural Strength
~20 N/mm2 (14 days, +23°C) | (According to EN 196) |
Tensile Strength
10 - 15 N/mm2 (14 days, +23°C) | (According to DIN EN ISO 527-3) |
Tensile adhesion strength
Time | Substrate | Bond strength |
After 3 days | Dry concrete | > 5 N/mm2 * |
After 3 days | Damp concrete | 5 N/mm2 * |
After 3 days | Steel blast cleaned | > 10 N/mm2 |
After 3 days | Brick dry | > 1.5 N/mm2 ** |
*100% concrete failure
**100% brick failure
Shrinkage
Hardens without shrinkage
Glass transition temperature
+49°C (7 days / +23°C) | (EN 12614) |
Application
Mixing Ratio
Part A : Part B = 1 : 1 by volume
Layer Thickness
0.5 mm min. / 10 mm max.
Sag Flow
Non-sag, suitable for overhead application
Ambient Air Temperature
+10°C min. / +35°C max.
Dew Point
Avoid condensation during dew point conditions. Substrate temperature during application must be at least 3°C above dew point.
Substrate Temperature
+10°C min. / +35°C max.
Substrate Moisture Content
Substrate must be dry or mat damp (no standing water)
Pot Life
60 minutes (at +23°C)
Curing Time
Temperature | Open Time | Curing Time |
+10°C | 210 minutes | 3 days* |
+20°C | 90 minutes | 2 days* |
+35°C | 45 minutes | 1 day* |
* to achieve approximately 80% of the performance
Minimum cartridge temperature +10°C
SUBSTRATE QUALITY
Mortar and concrete must be older than 28 days.
Adequate substrate strength (concrete, masonry, natural stone) must always be confirmed.
MIXING
Getting the Cartridge Ready:
- Unscrew and remove the cap.
- Pull out the plug.
- Screw on the static mixer.
- Place the cartridge into the gun and start application.
IMPORTANT NOTE: When the work is interrupted, the static mixer can remain on the cartridge after the gun pressure has been relieved. If the resin has hardened in the nozzle when work is resumed, a new nozzle must be attached.
CLEANING OF TOOLS
Clean all tools and application equipment with Sika® Thinner C immediately after use. Hardened / cured material can only be mechanically removed.