Product Data Sheet Show all documents
Sikaplan® SGK-15

Sikaplan® SGK-15

Polymeric membrane for adhered roof waterproofing

Sikaplan® SGK-15 is a multi-layer, synthetic roof waterproofing sheet based on premium-quality polyvinyl chloride (PVC) with inlay of glass non-woven and polyester fleece backing according to EN 13956.

  • Resistant to permanent UV irradiation
  • High dimensional stability due to glass fleece inlay
  • High water vapour permeability
  • Resistant to all common environmental influences
  • Compatible to old bitumen due to felt backing
  • Hot air welding without use of open flames
  • Recyclable
 
Contact Us
Product Data Sheet Show all documents

Usage

Roof waterproofing membrane for exposed flat roofs:
  • Partially adhered by correct Sika® adhesives.

Advantages

  • Resistant to permanent UV irradiation
  • High dimensional stability due to glass fleece inlay
  • High water vapour permeability
  • Resistant to all common environmental influences
  • Compatible to old bitumen due to felt backing
  • Hot air welding without use of open flames
  • Recyclable
 

Packaging

Packing unit:see price list
Roll length:

15.00 m

Roll width:2.00 m
Roll weight:63.00 kg

Colour

Surface:

slightly structured

Colours:

Top surface:

light grey (nearest RAL 7047)

lead grey (nearest RAL 7012)

Bottom surface:dark grey

Top surface of sheet in other colours available on request, subject to minimum order quantities.

Product Details

Sustainability / Certifications / Approvals

APPROVALS / STANDARDS

  • BBA Agrement Certification (09/4668).
  • EN13501-5 Broof(t4) as part of system.  
  • Polymeric sheets for roof waterproofing according to EN 13956, certified by notified body 1213-CPD-4125 and provided with the CE marking.
  • Reaction to fire according to EN 13501-1.
  • External fire performance tested according to ENV 1187 Brooft4 and classified according to BS:476 Part 3.
  • Official Quality Approvals and Agrement Certificates and approvals.
  • Monitoring and assessment by approved laboratories.
  • Quality Management system in accordance with EN ISO 9001/14001.
  • Production according to Responsible Care policy of Chemical Industry.
Product Information

Product Declaration

EN 13956

Shelf Life

Product does not expire if correctly stored.

Storage Conditions

Rolls must be stored in a horizontal position on pallet and protected from direct sunlight, rain and snow. Do not stack pallets of rolls during transport or storage.

Visible Defects

Pass

(EN 1850-2)

Length

15.00 m (-0 % / +5 %)

(EN 1848-2)

Width

2.00 m (-0.5 % / +1 %)

(EN 1848-2)

Effective Thickness

1.5 mm (-5 % / +10 %)

(EN 1849-2)

Straightness

≤  30 mm

(EN 1848-2)

Flatness

≤  10 mm

(EN 1848-2)

Mass per unit area

2.1 kg/m² (- 5 % / + 10 %)

(EN 1849-2)
System information

Compatibility

The PVC compound is not compatible with direct contact to other plastics, e.g. EPS, XPS, or PF.

The PVC compound is not resistant to tar, bitumen, oil and solvent containing materials.
Technical Information

Resistance to Impact

hard substrate≥  700 mm
soft substrate≥  1500 mm

Hail Resistance

rigid substrate

≥  22 m/s

flexible substrate

≥  30 m/s

Tensile Strength

longitudinal (md)1)

≥  600 N/50 mm

transversal (cmd)2)

≥  600 N/50 mm

1) md = machine direction
2) cmd = cross machine direction

Elongation

longitudinal (md)1)

≥  50 %

transversal (cmd)2)

≥  50 %

1) md = machine direction
2) cmd = cross machine direction

Tear Strength

longitudinal (md)1)

≥  150 N

transversal (cmd)2)

≥  150 N

1) md = machine direction
2) cmd = cross machine direction

Joint Peel Resistance

≥  300 N/50 mm

(EN 12316-2)

Joint Shear Resistance

≥  500 N/50 mm

(EN 12317-2)

Dimensional Stability

longitudinal (md)1) ≤  |0.3| %
transversal (cmd)2)≤  |0.3| %

Foldability at Low Temperature

≤  -25 °C

(EN 495-5)

Water Tightness

Pass

(EN 1928)

 

Effect of Liquid Chemicals, Including Water

On request

(EN 1847)

UV Exposure

Pass (> 5 000 h / grade 0)

(EN 1297)

External Fire Performance

BROOF(t4) ≥ 10°

(EN 13501-5)

Reaction to Fire

Class E

(EN ISO 11925-2, classification to EN 13501-1)

Application

Application Information

Ambient Air Temperature

-15 °C min. / +60 °C max. for hot air welding
+5 °C min. / +60 °C max. for cold welding

Substrate Temperature

-25 °C min. / +60 °C max. for hot air welding
+5 °C min. / +60 °C max. for cold welding
Application steps

SUBSTRATE QUALITY

The substrate surface must be uniform, smooth and free of any sharp protrusions or burrs, etc.
The Polyester fleece laminated to Sikaplan® SGK-15 underside separates sufficiently from any incompatible substrate. It prevents from direct contact to bitumen or plastic material, e.g. expanded polystyrene (EPS), extruded polystyrene (XPS), polyurethane (PUR), polyisocyanurate (PIR) or phenolic foam (PF) for compatibility in the built-up.

APPLICATION

Installation works must be carried out only by trained Sika Roofing Contractors. Installation of some ancillary products, e.g. contact adhesives/thinners is limited to temperatures above +5 °C. Please refer to the respective Product Data Sheets. Special measures may be compulsory for installation below +5 °C ambient temperature due to safety requirements in accordance with national regulations.

 

Documents