Parex® MONOGRIS E

Parex® MONOGRIS E

One Coat Grey Base Coat Render

A grey base coat/finishing coat and preparatory key coat render for variable and / or high or low suction substrates.

  • Suitable for diesel and electric spray machines
  • Excellent adhesion properties
  • Semi-lightweight render suitable for multiple substrates
Contact Us
Product Data Sheet Safety Data Sheet Show all documents

Usage

A high performance polymer modified, weather resistant, grey base coat and finishing  render for vertical external and internal walls. Suitable for equalising suction on mixed substrates and as a bonding base coat on to high or low suction substrates.
Suitable as a grey coat finishing render or as a base coat for receiving a Parex decorative finish. e.g. MONOREX GM & GF, MONOBLANCO, REVLANE, CRYLANE.  

Advantages

  • Suitable for diesel and electric spray machines
  • Excellent adhesion properties
  • Semi-lightweight render suitable for multiple substrates

Packaging

25 kg bags

Product Details

Product Information

Composition

Hydraulic mortar containing:
Cement, lime, siliceous and calcareous sands, mineral pigments and specific admixtures.

Shelf life

12 Months from date of manufacture

Storage conditions

Dry frost free conditions

Grain size distribution

Granulometry: 0 - 1.6 mm
Technical Information

Compressive strength

CS II

Capillary absorption

W2

Reaction to fire

A1

Application

Application Information

Mixing ratio

5.4-6.3 L per 25 kg bag
Consumption

Consumption

COVERAGE
Coverage is provided as guidance only, excludes wastage and will vary subject to substrate conditions and thickness applied.
Approx 1.25 - 1.3 m2 @ 15 mm/25 kg bag
Approx 6.7 m2 @ 2 - 3 mm/25kg bag
Application steps

EQUIPMENT

EQUIPMENT REQUIRED

Application by machine

Spray Render Machine

Constant Mix and Pump Machine

Pump Pressure

10-12 bar (water)

2.5-6 bar/360 water flow L/hr

Pumping distance/height

Up to 120 m/60 m approx

Up to 50 m/30 m approx

Power Source

Diesel

Electric 

APPLICATION

  • Refer to Substrate Preparation first

SUITABLE FOR

  • Machine or manual applications

KEY COAT APPLICATION

  • Spray apply a stippled 2-3 mm layer leaving a well textured stippled surface.
  • Hand apply a 2-3 mm thick layer to the substrate and using a toothed trowel or a heavy duty and well laiden roller, texture the surface to leave a combed effect or stippled finish respectively.
  • Ensure the product is mixed correctly with the correct water content and do not allow the render to cure too quickly as surface holes in the render could occur.
  • Avoid applying large areas of the key coat before creating the stippled or toothed trowel finish when applying by hand.

TO RECEIVE A ONE-COAT FINISHING COAT E.G. MONOREX, MONOBLANCO, ETC

  • Spray or hand apply, leaving a ruled, level toothed trowel finished minimum thickness of 6 - 8 mm.

TO RECEIVE A PAINT COATING E.G. DPR COATING OR DPR/REVLANE+ COATINGS:

  • Spray or hand apply a ruled and level 7 - 8  mm base coat and leave with a toothed trowel finish. When the base coat has dried, apply a second layer of 7 - 8 mm thickness and trowel and level smooth.
  • The covering thickness must be a minimum of 15mm at all points.

MONOGRIS E can be left as a finished coat though evenness of colour is not guaranteed.

ASSOCIATED DECORATIVE COVERINGS

SURFACE CONDITION OF MONOGRIS E

CURING TIME BEFORE COVERING

MONOREX GM, MONOREX GF

MONOBLANCO

PARLUMIERE FIN/MOYEN

PAREXAL

Other Parex coatings may be suitable.

STIPPLED COAT OR NOTCHED TROWEL

A  top coat finish can be applied as soon as the base coat has initially cured. 

When the base coat has been left to cure in excess of 3 days, dampen the surface prior to applying the top coat.

If the base coat has been left to dry for some time it is recommended a preparation coat of MICRO GOBETIS 3000 is used

REVLANE finishes

Paints

Thick synthetic coatings  

Whitewashes, lime paints

FLOAT FINISH**

Minimum 3 weeks.

** Ensure aircrete blocks are fully dry

before applying MONOGRIS E as block shrinkage could occur and this may crack the render if applied on a wet substrate.

                                                                                                                                                                                                                                

MAXIMUM THICKNESS OF MONOGRIS E

ULTRA-LIGHTWEIGHT, LIGHTWEIGHT & DENSE AGGREGATE CONCRETE BLOCKS, CLAY BLOCKS, BRICKS

STANDARD LOW AND NORMAL DENSITY LIGHTWEIGHT AIRCRETE BLOCKSSHUTTERED CONCRETE

25 mm 

20 mm

15 mm