Parex Tecgrip S

Cementitious anchoring and stitching grout

Parex Tecgrip S is a cementitious anchor grout requiring only the addition of clean water. The product is based on a Portland cement mix with high quality graded silica sands plus a synergistic blend of admixtures.
The mixed grout is pumped into place using a Pumpable mortar cartridge gun. Each filling of the gun must be used within 5 minutes to avoid thickening. The product in the mixing vessel must be mixed each time a gun filling is carried out.
The injected grout will tighten in the anchor hole and fix the bolt, tie or other unit into the substrate. Tecgrip S is suitable for fixings into most construction materials including concrete, rock, brickwork, masonry blockwork or other substrates capable of carrying the design load.  

  • Single component, just add water.
  • Conforms to EN 998-2.
  • Consistency: thixotropic mortar.
  • Minimum annular clearance 2mm.
  • Hand or mechanical pump placed.
  • Suitable for vertical application.
Product Data Sheet Show all documents

Usage

  • Ties into brick arches.
  • Overhead rail tracks.
  • Starter bars and dowels.
  • Brick ties and stitching.
  • Anchoring.

Advantages

  • Single component, just add water.
  • Conforms to EN 998-2.
  • Consistency: thixotropic mortar.
  • Minimum annular clearance 2mm.
  • Hand or mechanical pump placed.
  • Suitable for vertical application.

Packaging

25kg bags

Colour

Grey powder

Product Details

Product Information

Chemical Base

Cementitious powder

Shelf Life

6 months from date of manufacturing

Storage Conditions

Store properly in dry conditions in undamaged and unopened original sealed packaging.

Maximum Grain Size

1.0mm

Density

~2050kg/m3

pH-Value

12.5

Total Chloride Ion Content

0.02%

(EN 196-2)

 
Technical Information

Compressive Strength

Duration

Compressive Strength

24 hours

~20 MPa

7 days

~50 MPa

28 days~60 MPa

All values tested in lab conditions at 20°C / 90% RH.

Modulus of Elasticity in Compression

~23 GPa

Tensile Strength

~3 MPa

Tensile adhesion strength

≥0.15 MPa

(EN 998-2)

Thermal Conductivity

P=50%1.11 [W/(m.K)]
P=90%1.21 [W/(m.K)]

(EN 998-2)

Water Absorption

0.135 kg/(m².min0.5)

(EN 1015-8)

Permeability to Water Vapour

15/35μ

Reaction to Fire

Euroclass A1

Application

Application Information

Mixing Ratio

1 part water to 5 parts powder (5 litres water per 25 kg bag)

Layer Thickness

3 mm min.

Ambient Air Temperature

+5°C min. / +35°C max.

Substrate Temperature

+5°C min. / +35°C max.

Open Time

~30 minutes at 20°C
Consumption

Yield

25kg yields approx. 15 litres mixed material
Application steps

MIXING

Pour 5 litres of clean water into a clean mixing vessel for each complete bag of Parex Tecgrip S. Slowly add the powder to the water whilst continually mixing. Mechanical mixing should be carried out using a high torque slow speed drill with a Grout Stirrer. Mix material for a further 2 minutes after all powder has been added to achieve a homogeneous mix.

APPLICATION

Load the mixed anchor grout into the cartridge of the injection gun. Use an extension tube for the cartridge to allow filling of the hole from the bottom to the mouth. Immediately after placing the Parex Tecgrip S, insert the bolt, bar, wall tie, slotting or other fixing. Gently agitate the inserted fixing to ensure complete contact by the anchor grout. Once placed do not disturb before the anchor grout has hardened.
Each cartridge filling should be used within 5 minutes. Prior to each cartridge loading, the material in the pail should be re-mixed to maintain grout workability.
For best tensile anchorage results, a minimum embedment depth of 100mm is recommended. Hole diameters may be varied but a minimum of 3mm all-round clearance should be used. This clearance may be increased for ease of placing fixings into deep holes.

Factors controlling uniaxial pull out load:

  • Type and strength of substrate.
  • Embedment depth.
  • Hole preparation.
  • Type of fixing.

CURING TREATMENT

Protect all exposed surfaces from premature drying. Standard curing treatments can be utilised such as damp hessian sheets, plastic sheets or suitable curing membrane such as Sika®Antisol MP10.

CLEANING OF TOOLS

Clean all tools and application equipment with water immediately after use. Hardened/cured material can only be mechanically removed.

 