SikaGrout®-212 Fluid

CEMENTITIOUS, HIGH FLOW, NON-SHRINK, GENERAL PURPOSE PRECISION GROUT
  • Easy to use (pre-bagged ready to mix powder). 
  • Pre-batched for quality. 
  • Just add water. 
  • Economical. 
  • Versatile - can be used for a variety of applications. 
  • High performance. 
  • High final strength. 
  • Shrinkage compensated (non-shrink). 
  • Fluid consistency. 
  • Consistency can be adjusted within the permissible water content range. 
  • No segregation or bleeding. 
  • Can be pumped long distances. 
  • Good fluidity, excellent for placement by pouring.
  • Self-levelling.
  • Free of chlorides and metallic particles (does not oxidise in contact with humidity; protects the metal against corrosion, due to its high pH). 
  • Slightly expansive.
  • Rapid, high mechanical resistance.
  • Excellent adhesion to concrete, mortar or steel. Provides a monolithic bond and resists shocks and vibrations.
  • Non-corrosive and non-toxic.
  • Fire rating and protection properties comparable to concrete (reaction to fire rating EuroClass A1). 

SikaGrout®-4800

(former MFlow 4800)
Metallic aggregate reinforced, ultra-high strength precision grout
  • Contains metallic aggregates to provide high strengths and increased impact resistance under dynamic and repetitive loading.
  • Very high early strengths shorten the waiting time for starting the machinery process.
  • Ultra-high final strengths allow very high compressive loading.
  • Provides solutions for various application details with wide application thickness: 20 to 150 mm.
  • Hardens without bleeding, settlement or drying shrinkage when mixed, placed and cured.
  • Can be used at temperatures down to +2 °C.
  • Designed for use where thermal movement of equipment and machinery and other effects of heating / cooling and wetting / drying are anticipated.
  • High flow for full compaction, even in areas with congested steelwork.
  • For hand or machine application.
  • Extra low shrinkage for durability.
  • Excellent freeze / thaw resistance.
  • Very low permeability to water and chlorides.
  • Sulphate-resistant.
  • CE Marked in accordance with EN 1504-6.

SikaGrout®-510 CS High Flow

High flow, non-shrink, high rapid strength, versatile (consistency can be adjusted), cementitious grout with sustainability benefits
  • Ready to use - just add water. 
  • Easy to mix and apply. 
  • High strength.
  • Excellent flow characteristics at the maximum permissible water content.
  • Non-shrink (shrinkage compensated). 
  • Non-metallic and 'chloride-free' (<0.05%).
  • Low water absorption.
  • Durable. 
  • No segregation or bleeding. 
  • Low permeability. 
  • Non-corrosive.
  • Resistance to sea water and mild alkali attack.
  • High flowability retention. 
  • Pumpable and pourable. 
  • Adjustable water content for varying applications.
  • Quality assured factory blend. 
  • Application thickness range 10 mm to 100 mm.
  • Uses supplementary cementitious materials (SCMs) for improved sustainability.
  • Reaction to fire EuroClass A1.

SikaGrout®-9800

High strength grout with applied nanotechnology for grouting offshore wind turbine installations
  • C90/105 concrete strength class according EN206 and DIN1045
  • Can be installed with a continuous mixing and pumping process. Typical output rates of ≥ 20 m³/hour per mixing unit.
  • Quick return to service and removal of temporary supports due to high early strength build-up. ≥ 40 MPa @ 24hrs at 20°C.
  • Very good strength gain at low temperatures.
  • No segregation or bleeding to ensure consistent physical performance inside the grouted connection, and to prevent pump blockages.
  • Excellent fatigue resistance
  • No wash-out during below water grouting.
  • Pump able over long distances and large heights.
  • Specially graded sands and exceptional flow and low friction increases pump output, reduces installation times and costs as well as reducing pump pressures and wear.
  • Available as silo material.

SikaGrout®-9200

(former MFlow 9200)
Ultra-high strength, cement based grout with applied nanotechnology for grouting onshore VESTAS wind turbine installations
  • Ultra-high compressive strength: > C100/115 according to EN 206-1
  • Ultra-high modulus for exceptional stiffening properties
  • Excellent fatigue resistance. 
  • Quick return to service and removal of temporary supports due to high early strength build-up ≥ 75 MPa @ 24hrs at 20°C
  • No segregation or bleeding to ensure consistent final physical performance and to prevent pump blockages
  • Extended pot life of ≥ 2 hours
  • Can be pumped into complex areas or areas inaccessible to conventional grouting methods
  • Specially graded sands and exceptional flow and low friction increases pump output, reduces installa-tion times and costs as well as reducing pump pres-sures and wear
  • Dust reduced for ease of handling
  • Cement based
  • Low chromate

SikaGrout®-9300

(former MFlow 9300)
Ultra high strength, cement based grout with metallic aggregate and applied nanotechnology for grouting onshore wind turbine installations  
  • Ultra high compressive strength >120 MPa.
  • Ultra high modulus for exceptional stiffening properties.
  • Excellent fatigue resistance. 
  • Quick return to service and removal of temporary supports due to high early strength build-up. ≥ 60 MPa @ 24hrs at 20°C
  • No segregation or bleeding to ensure consistent final physical performance and to prevent pump blockages. 
  • Contains metallic aggregates to provide increased resistance to dynamic and repetitive loading
  • Pump able over long distances and large heights.
  • Extended pot life of ≥ 2 hours
  • Can be pumped into complex areas or areas inaccessible to conventional grouting methods
  • Specially graded sands and exceptional flow and low friction increases pump output, reduces installa-tion times and costs as well as reducing pump pres-sures and wear
  • Dust reduced for ease of handling
  • Cement based.
  • Low chromate.  

SikaGrout®-9500

Ultra-high strength, high modulus, cement based grout with applied nanotechnology for grouting offshore wind turbine installations
  • Certified by Det Norske Veritas (DNV)
  • Ultra-high mean compressive strength ≥135MPa.
  • Ultra-high modulus for exceptional stiffening properties.
  • Very good fatigue resistance.
  • Quick return to service and removal of temporary supports due to high early strength build-up. ≥ 60 MPa @ 24hrs at 20°C
  • Excellent strength gain at low temperatures @ 0°C at 24hrs
  • No segregation or bleeding to ensure consistent final physical performance and to prevent pump blockages
  • No wash-out during below water grouting
  • Pump able over long distances and large heights.
  • Extended pot life of ≥ 4 hours
  • Specially graded sands and exceptional flow and low friction increases pump output, reduces installation times and costs as well as reducing pump pressures and wear Dust reduced for ease of handling and safety of workers
  • Available in special, watertight big bags for large scale application.
  • Meets the requirements of EN1504-6 for anchoring reinforcement bars.