Product Data Sheet Show all documents
Parex CS Grout

Parex CS Grout

Non-shrink, high strength, versatile (consistency can be adjusted), high flow, cementitious grout

Parex CS Grout is a Portland cement based product giving high strength, high flow and non-shrink properties. By adjusting the water content, different consistencies (liquid, plastic and mortar) can be achieved. Placed grout gives structural support and good vibration resistance.

  • High strength.
  • High flow at the maximum permissible water content. 
  • Non-shrink.
  • 'Chloride-free' (<0.05%).
  • Low water absorbtion.
  • Resistance to sea water and mild alkali attack.
  • Excellent flow characteristics.
  • Pumpable.
  • Adjustable water content for varying applications.
Contact Us
Product Data Sheet Show all documents

Usage

  • Crane rail tracks.
  • Stanchion bases.
  • Machine bed plates.
  • Dowel bars between precast units.
  • Ground anchors.
  • Bridge bearing supports.
  • Void filling.  

Advantages

  • High strength.
  • High flow at the maximum permissible water content. 
  • Non-shrink.
  • 'Chloride-free' (<0.05%).
  • Low water absorbtion.
  • Resistance to sea water and mild alkali attack.
  • Excellent flow characteristics.
  • Pumpable.
  • Adjustable water content for varying applications.

Packaging

25 kg bags and 1000 kg bulk bags

Colour

Grey powder

Product Details

Sustainability / Certifications / Approvals

CERTIFICATES AND TEST REPORTS

Parex CS Grout has been tested in accordance with the appropriate parts of the following standards: EN 12390; BS 476; ASTM C953; ASTM  and C1107. 
Parex CS Grout complies with the requirements of Corps of Engineers Specification for Non-Shrink Grout CRD C621, BS 6920 and the Specification for Highway Works Clause 2601 - Bedding Mortar.
Product Information

Shelf life

9 months from date of manufacture (25 kg bags)

6 months from date of manufacture (1000 kg bulk bags)

Storage conditions

Store properly in dry conditions in undamaged and unopened original sealed packaging

Density

2100 kg/m3

 
Technical Information

Compressive strength

Consistency

1 Day

3 Days

7 Days

28 Days

Mortar

~50 N/mm2

~66 N/mm2

~72 N/mm2

~75 N/mm2

Plastic

~41 N/mm2

~60 N/mm2

~69 N/mm2

~72 N/mm2

Liquid

~25 N/mm2

~47 N/mm2

~51 N/mm2

~56 N/mm2

Modulus of elasticity in compression

~30 KN/mm2

Flexural-strength

~10 N/mm2 (after 28 days)

*All testing is carried out in lab conditions at 20°C. Results may vary in site conditions.

Application

Application Information

Layer thickness

10 mm minimum / 100 mm maximum

Ambient air temperature

+5°C minimum / +35°C maximum

Initial set time

~260 minutes

Final set time

~290 minutes
Consumption

Yield

25 kg yields ~13.25 litres of grout

1000 kg yields ~530 litres of grout
Application steps

MIXING

Pour 4.5 litres of clean water into the mixing vessel for each complete 25 kg bag of Parex CS Grout to be used. Slowly add the powder to the water whilst continually mixing. Mechanical mixing should be carried out using either a high torque slow speed drill with a grout stirrer, or a grout mixer set on slow speed (high speed or colloidal mixing will cause thixotropy, leading to loss of flow). 

Varying consistencies are achievable using the following water contents per 25 kg bag:

Mortar

3.6 litres

Plastic

4.3 litres

Liquid

4.8 litres

APPLICATION

Grout should be placed within 20 minutes of mixing. Continuous placing is important, pouring from one side of the formwork until the grout appears at the opposite side of the grouting area. Do not disturb once grouting has been completed.  

CURING TREATMENT

Placed grout, which is exposed, should be cured in accordance with good concrete practice, including water spray or by using Sikafloor® ProSeal. In cold weather, apply heat blankets to maintain a constant temperature.

CLEANING OF EQUIPMENT

Clean all tools and application equipment with water immediately after use. Hardened / cured material can only be mechanically removed.