Sikafloor® TC 681

(former MSeal TC 681)

2-Part Polyaspartic top coat, pigmented, glossy, fast and low temperature curing, UV-stable, for car parking systems and broadcasted coatings

Sikafloor® TC 681 is a two component, pigmented, fast and low temperature curing, UV-stable, non yellowing, elastic top coat with glossy finish on broadcasted coatings. Sikafloor® TC 681 contains solvents.

  • rapid cure
  • short „ready for traffic“ times
 
  • excellent mechanical properties
  • hard wearing
  • elastic
  • crack bridging
  • excellent UV- and weather resistance
  • attractive appearance
  • low dirty retention
  • easy to clean and maintain
Contact Us
Product Data Sheet Show all documents

Usage

Sikafloor® TC 681 is primarily intended as the top coat in car park deck applications where its rapid cure, low dirt retention, excellent UV resistance and excellent wear properties can be exploited.

Advantages

  • rapid cure
  • short „ready for traffic“ times
 
  • excellent mechanical properties
  • hard wearing
  • elastic
  • crack bridging
  • excellent UV- and weather resistance
  • attractive appearance
  • low dirty retention
  • easy to clean and maintain

Packaging

Sikafloor® TC 681 is supplied in 28 kg working packs.

Colour

Sikafloor® TC 681 is available in following colours:    approx. RAL 1001, 1015, 6021, 7001, 7016, 7023, 7030, 7032, 7035, 7038, 7040. For further colours consult your local sales office.

Product Details

Sustainability / Certifications / Approvals

APPROVALS / STANDARDS

CE marking and declaration of performance based on EN 13813:2002 Screed material and floor screeds — Screed material — Properties and requirements — Synthetic resin screed material.

CE marking and declaration of performance based on EN 1504-2:2004 Products and systems for the protection and repair of concrete structures — Surface protection systems for concrete — Coating.
Product Information

Chemical Base

Polyaspartic

Shelf Life

Under the specified storage conditions the material has a shelf life of 12 months. For maximum shelf life under these conditions see "Best before" label.

Storage Conditions

Store in original containers under dry conditions at a temperature between 15 – 25 °C. Do not expose to direct sunlight.

Density

Part A

1,74 g/cm3

Part B

1,07 g/cm3

Solid content by mass

94%
Technical Information

Tensile Strength

Cured 28 days at 23°C

20 N/mm2

Tear Strength

Cured 28 days at 23°C

70 N/mm2

(DIN 53515)

Application

Application Information

Mixing Ratio

100 : 67

Ambient Air Temperature

Min. at 23°C

8°C

Max. at 23°C

30°C

Relative Air Humidity

Max.

80%

Substrate Temperature

Min. at 23°C

8°C

Max. at 23°C

30°C

Pot Life

at 23°C

25 min.

Curing Time

Ready for pedestrian traffic at 23°C

4 h

Ready for car traffic at 23°C

7 h

Fully cured at 23°C

7 d
Consumption

Consumption

Approx. 0.6 – 0.9 kg/m2 depending on the size and distribution of the aggregate used in the wear coat.
Application steps

SUBSTRATE PREPARATION

The coating to which Sikafloor® TC 681 is to be applied to should be clean and dry and free of any substances which may impair adhesion. Application should take place within the re-coat intervals of the coating to which it is to be applied.

MIXING

Sikafloor® TC 681 is supplied in working packs which are pre-packaged in the exact ratio. Before mixing, precondition both the A and B components to a temperature of approximately 15 to 25 °C.

Pour the entire contents of Part B into the container of Part A. DO NOT MIX BY HAND. Mix with a mechanical drill and paddle at a low speed (approx. 300 rpm) for at least 3 minutes. Scrape the sides and the bottom of the container several times to ensure complete mixing. Keep the mixer bladed fully submersed in the coating to avoid introducing air bubbles. DO NOT WORK OUT OF THE ORIGINAL CONTAINER. After proper mixing to a homogeneous consistency, pour the mixed Parts A and B into a clean container and mix for a further minute.

 

APPLICATION

Sikafloor® TC 681 is poured onto the prepared substrate and spread with a notched trowel, or spreader and back rolled using a medium nap lambs wool roller.

The curing time of the material is influenced by the ambient, material and substrate temperatures. At low temperatures, the chemical reactions are slowed down; this lengthens the pot life, open time and curing times. High temperatures speed up the chemical reactions thus the time frames mentioned above are shortened accordingly. To fully cure, the material, substrate and application temperature should not fall below the minimum during application and for at least 2 hours after application. Following application the material should be protected from direct contact with water for approx. 2 hours. The temperature of the substrate must be at least 3 K above the dew point both during the application and for at least 2 hours after application (at 15 °C).

CLEANING OF TOOLS

Clean all tools and application equipment with Sika® Thinner C immediately after use. Hardened material can only be removed mechanically.