Sikagard®-850 Clear
Permanent Clear Anti-graffiti and Anti-fly Poster Coating
Sikagard®-850 Clear is a one-part ready to use, polyorganosiloxane based, permanent anti-graffiti and anti-fly poster semi-matt coating. This product is part of the Sikagard® Anti-graffiti System.
- Ready to use - no dilution with solvent necessary at the job site.
- Permanent - graffiti can be typically removed more than 50 times without damaging the protection, or requiring a refresher coat, when using non-aggressive cleaning techniques.
- Poster prevention – fly poster does not bond onto protected substrate or can be easily removed, even after many cleaning cycles.
- Semi-matt aspect. Clear aspect when using the fair-faced concrete build-up.
- No chemical agents required for cleaning.
- Cleaning requires only cold-water pressure (80 to 100 bar) or cold-water low pressure washing and rubbing down with a clean cloth or scrubbing brush.
- Water vapour permeable.
- Complies with the requirements of EN 1504-2 as protective coating.
- Low water absorption.
- Very good resistance against weathering and ageing.
- Good resistance to UV exposure.
- Applied by brush, roller or airless spray.
- Very low dirt pick-up.
Usage
As a permanent anti-graffiti and anti-fly poster coating on the following substrates:- Fair faced concrete, masonry, cementitious render.
- Coated concrete, masonry, cementitious render.
- Coated concrete, masonry, cementitious render previously treated with a hydrophobic impregnation.
- Coated or uncoated wood.
- Moisture control (Principle 2, method 2.3 of EN 1504-9).
- Increasing the resistivity (Principle 8, method 8.3 of EN 1504-9).
Advantages
- Ready to use - no dilution with solvent necessary at the job site.
- Permanent - graffiti can be typically removed more than 50 times without damaging the protection, or requiring a refresher coat, when using non-aggressive cleaning techniques.
- Poster prevention – fly poster does not bond onto protected substrate or can be easily removed, even after many cleaning cycles.
- Semi-matt aspect. Clear aspect when using the fair-faced concrete build-up.
- No chemical agents required for cleaning.
- Cleaning requires only cold-water pressure (80 to 100 bar) or cold-water low pressure washing and rubbing down with a clean cloth or scrubbing brush.
- Water vapour permeable.
- Complies with the requirements of EN 1504-2 as protective coating.
- Low water absorption.
- Very good resistance against weathering and ageing.
- Good resistance to UV exposure.
- Applied by brush, roller or airless spray.
- Very low dirt pick-up.
Packaging
5 and 20 kg containers (refer to current price list for packaging variations).
Colour
Final applied finish: Semi-matt / clear.
NOTE: 'Fair Face System' will result in a clear aspect, similar in appearance to the untreated substrate.
Product Details
APPROVALS / STANDARDS
- CE marking and Declaration of Performance (Ref. 31191591) based on EN 1504-2:2004 Products and systems for the protection and repair of concrete structures — Surface protection systems for concrete — Coating.
- Adhesion after thermal compatibility EN 13687-1:2002 (100 cycles of freeze and thaw with de-icing salts) and EN 13687-2:2002 (10 cycles of thunder shower) - Applus Laboratories, Spain, Report Nber 21/32304762.
- 50 cleaning cycles UNE-EN ISO 2409, Sikagard®-552 W + Sikagard®-850 Activator + Sikagard®-850 Clear, Applus, No. 23/32304334.
- 50 cleaning cycles UNE-EN ISO 2409, Sikagard®-850 Primer + Sikagard®-850 Clear, Applus, No. 22/32306109.
Chemical Base
Polyorganosiloxanes polymer and solvent
Shelf Life
12 months from date of production.
Storage Conditions
The product must be stored in original, unopened and undamaged packaging in dry conditions at temperatures between +5 °C and +35 °C. Always refer to packaging.
Density
~0.92 g/cm3
Viscosity
~580 mPa·s (at +20 °C)
~430 mPa·s (at +40 °C)
Volatile organic compound (VOC) content
~350 g/L (calculated)
System Structure
System Component | Product |
Primer for Uncoated Mineral Substrates | Sikagard®-850 Primer |
Primer for Coated Mineral Substrates or Coated Wood | Sikagard®-850 Activator |
Top Coat | Sikagard®-850 Clear |
When applied to bare mineral surface, Sikagard®-850 Clear may provide a wet look effect. To reduce/eliminate this effect, the following build-up is recommended (known as the 'Fair Face System'):
Sikagard®-552 W Aquaprimer + Sikagard®-850 Activator + Sikagard®-850 Clear.
Freeze Thaw De-Icing Salt Resistance
>1.8 MPa | EN 13687-2 |
No bubbles, cracks or surface defects after weathering.
Tests were performed after 100 cycles instead of 50 cycles as required by EN 1504-2.
Permeability to Water Vapour
SD = 0.28 m | EN ISO 7783-1/2 |
Conforms to Class I (<5 m)
Capillary Absorption
0.0026 kg/m2*h0.5 | EN 1062-3 |
NOTE: "a" of Table 5 of EN 1504-2: "When the capillary absorption to water is <0.01 kg/m2*h0.5 the diffusion of chloride ions is not to be expected".
Application
Layer Thickness
~140 to 270 μm (wet film thickness)
Ambient Air Temperature
+8 °C minimum / +35 °C maximum
Relative Air Humidity
≤ 80 %
Dew Point
Substrate and ambient temperature must be at least +3 °C above dew point.
Applied Product Ready for Use
Final Drying | Up to ~24 hours at +20°C for thick film build-up |
Full Cure | ~7 days |
Times are approximate and will be affected by film thickness and changing ambient conditions particularly temperature and relative humidity.
Anti-graffiti and anti-poster protection is achieved as soon as the coating has dried out (~24 hours).
Consumption
NOTE: Generally, one coat is sufficient on a suitably prepared, uniform and primed substrate.
Top Coat: ~125 to 250 g/m2
These figures are theoretical and do not allow for any additional material due to surface porosity, surface profile, variations in level, wastage or any other variations. Apply product to a test area to calculate the exact consumption for the specific substrate conditions and proposed application equipment.
APPLICATION
Strictly follow installation procedures as defined in method statements, application manuals and working instructions which must always be adjusted to the actual site conditions.
IMPORTANT
Existing coatings must be tested to confirm their compatibility with Sikagard®-850 Activator and Sikagard®-850 Clear.
PRIMER / ACTIVATOR
IMPORTANT
On rough substrates, use a brush to apply Primer and make sure the Primer covers all the surface including voids.
IMPORTANT
Allow the Primer surface to dry and become tack-free before applying the top coat (~2 to 3 hours, depending on weather conditions).
IMPORTANT
Allow Sika® MonoTop® mortars to cure for 3 to 5 days before applying Primer.
Substrate (Mineral) Without Existing Coating or Hydrophobic Impregnation (including Sika® MonoTop® products)
- Apply Sikagard®-850 Primer evenly over the prepared substrate at the required consumption rate. Always refer to Product Data Sheets.
-
The Primer must be continuous and pore ('holiday') free.
Substrate (Mineral or Wood) with Existing Coating / Lasure
- Apply Sikagard®-850 Activator evenly over the prepared substrate at the required consumption rate. Always refer to Product Data Sheets.
- The Activator must be continuous and pore ('holiday') free.
Substrate with Hydrophobic Impregnation
- Prime with Sikagard®-850 Primer evenly over the prepared substrate at the required consumption rate. Always refer to Product Data Sheet.
- The Primer must be continuous and pore ('holiday') free.
Wood (Uncoated)
No priming is required.
To Achieve the 'Fair Face System'
- Apply a thin, even layer of Sikagard®-552 W Aquaprimer to reduce the 'wet-look' resulting finish. Do NOT use thick pile rollers or brushes to apply, as excessively thick application can result in unsightly white stains. Always refer to Product Data Sheets.
- Apply Sikagard®-850 Activator evenly over the prepared substrate at the required consumption rate. Always refer to Product Data Sheets.
- The Activator must be continuous and pore ('holiday') free.
TOP COAT
IMPORTANT
If applied over the Primer or Activator, refer to appropriate drying time / waiting time before overcoating.
Application by Brush or Medium to Long Hair Roller
- If required, mix the coloured pigment into the product until fully dispersed and a uniform colour is achieved.
- Apply the Product evenly over the surface.
- The coating must be continuous, pore ('holiday') free and to the required surface finish.
- Protect the freshly applied coating from heavy rain or rain showers until dry to prevent surface damage.
Application by Airless Spray
IMPORTANT
Do NOT use aerosol car body type spraying equipment.
NOTE: The airless spray may not give a smooth or acceptable finish. It may be necessary to back-roll the coating with a roller to ensure a suitable finish and film build-up.
Requirement: Airless spraying characteristics:
- Pressure: 220 to 250 bar (3200 to 3600 psi).
- Hose diameter: ~10 mm (3/8").
- Tip size: 0.013" to 0.017" (0.33 to 0.43 mm).
- Fan width: selected accordingly for the tip size (e.g. 6" or 8" for 0.013" tip, 8" or 10" for 0.015" tip, and 10" for 0.017" tip).
- Sprayer: should be selected appropriately for the tip size.
- Filter: 60 mesh.
- If required, mix the coloured pigment into the product until fully dispersed and a uniform colour is achieved.
- Spray apply the Product in a continuous operation and at a speed to achieve a consistent thickness.
- The coating must be continuous, pore ('holiday') free, and to the required surface finish.
- Protect the freshly applied coating from heavy rain or rain showers until dry to prevent surface damage.
NOTE: Always follow the equipment manufacturer's recommendations and instructions for use.
CLEANING OF TOOLS
- Clean all tools and application equipment with Sika® Thinner C immediately after use. Hardened material can only be mechanically removed.
- Clean airless spray equipment at regular intervals to prevent hardened silicon particles blocking the spraying tip.
CLEANING
Graffiti Removal
IMPORTANT
Do NOT use rotating nozzle on high-pressure cleaning equipment.
As a general rule, always remove graffiti as soon as possible using either of the two options:
- Cold-water high-pressure jetting / cleaning equipment (~80 bar / 1200 psi) from a distance of ~10 cm from the substrate.
- Cold-water low pressure washing and rubbing down with a suitable absorbent clean cloth or a soft scrubbing brush.
Poster Removal
Posters applied with water-based paste glues, do not bond on substrates treated with Sikagard®-850 Clear. They will either fall off under their own weight or can easily be removed with minimal effort.
Kindly discard them properly in a recycling center (in accordance with local requirements).