Sikagard®-675 W GB ElastoColor
Sikagard®-675 W GB ElastoColor is a one-part, plasto-elastic water dispersed coating based on styrene acrylate dispersion for the protection and enhancement of fair-faced concrete. Sikagard®-675 W GB ElastoColor can be applied over existing coatings or directly onto the concrete surfaces. Sikagard®-675 W GB ElastoColor complies with the requirements of EN 1504-2 as a protective coating.
- Water vapour permeable.
- Resistant to weathering and ageing.
- Application by roller brush or spray.
- High covering power (good opacity).
- Prevents water ingress.
- High diffusion resistance to CO2 (carbon dioxide).

Usage
- Protection and enhancement of concrete structures.
- Concrete repair works on Sika® levelling mortar, fibre cement and overcoating existing soundly adhering coatings.
- Suitable for protection against ingress (Principle 1, method 1.3 of EN 1504-9).
- Suitable for moisture control (Principle 2, method 2.3 of EN 1504-9).
- Suitable for increasing the resistivity (Principle 8, method 8.3 of EN 1504-9).
Advantages
- Water vapour permeable.
- Resistant to weathering and ageing.
- Application by roller brush or spray.
- High covering power (good opacity).
- Prevents water ingress.
- High diffusion resistance to CO2 (carbon dioxide).
Packaging
15 l pails
Colour
Thixotropic liquid available in almost every colour shade (minimum order requirements may apply).
Product Details
APPROVALS / STANDARDS
Conforms to the requirements of EN 1504-2.
Reaction to fire classification B-s1, d0 in accordance with BS EN 13501-1:2018.
Complies with the requirements of A2-s1,d0 reaction to fire in accordance with BS EN 13501-1:2018 (please contact Sika Technical Services for more information on system build up requirements).
Chemical Base
Styrene acrylate dispersionShelf Life
12 months
Storage Conditions
Store in cool and dry conditions. Protect from direct sunlight and frost.
Density
~1.42 kg/l (at +20 °C)
Solid content by mass
~64 %
Solid content by volume
~48 %
System Structure
Normal absorbent concrete and/or well cured thin layer Sika renders (Sika MonoTop®-3020, etc.):
System | Product | Number of Coats |
Priming | Sikagard®-675 W GB ElastoColor diluted with ~15% H2O (water) | 1 |
Smooth non-absorbent concrete:
System | Product | Number of Coats |
Priming | Sikagard®-551 S Elastic Primer | 1 |
Absorbent fair-faced concrete:
System | Product | Number of Coats |
Priming | Sikagard®-552 W Aquaprimer | 1 |
Water splash zones, de-icing salt exposure:
System | Product | Number of Coats |
Priming | Sikagard®-705 L or other Sika® hydrophobic impregnation (EN 1504-2 Penetration Depth Class II) | 1-2 |
Varied types of substrates - dense or weak tensile strength < 1 MPa:
System | Product | Number of Coats |
Priming | Sikagard®-551 S Elastic Primer | 1 |
All substrates:
System | Product | Number of Coats |
Top Coat* | Sikagard®-675 W GB ElastoColor | 2 |
Note:
- With yellow or red colour shade variations and/or dark substrates, more than two coats may be required. Trials are advised.
- Refer to relevant Product Data Sheets within the system.
Tensile adhesion strength
~ 2.7 MPa | (EN 1542) |
Capillary Absorption
w = 0.07 kg/(m2h0.5) | (EN 1062-3) |
Diffusion Resistance to Water Vapour
Dry film thickness | d = 270 μm |
Equivalent air layer thickness | SD, H2O = 0.59 m |
Water vapour permeability | 35.6 g/m2/day |
Requirements for breathability | SD, H2O ≤ 5 m |
Permeability to CO2
Dry film thickness | d = 160 μm |
Equivalent air thickness | SD, CO2 = 235 m |
Diffusion coefficient CO2 | μCO2 = 1.47x 106 |
Requirements for protection | SD, CO2 ≥ 50 m |
Behaviour after Artificial Weathering
Pass after 2000 hours
Reaction to Fire
B-s1, d0 | (BS EN 13501-1:2018) |
As part of a system A2-s1,d0 is achieveable (please contact Sika technical services for system build up information).
Application
Layer Thickness
Minimum required dry thickness to achieve full durability characteristics (CO2 diffusion, adhesion after thermal cycling, etc.) ≈ 160 microns.
Ambient Air Temperature
+8 °C minimum / +35 °C maximum
Relative Air Humidity
<80 %
Dew Point
Substrate and ambient temperature must be at least 3 °C above dew point.
Substrate Temperature
+8 °C minimum / +35 °C maximum
Waiting Time / Overcoating
Waiting time between coats at +20 °C substrate temperature:
Previous coating | Waiting time (Hours) | Next coating |
Sikagard®-552 W Aquaprimer | >12 | Sikagard®-675 W GB ElastoColor |
Sikagard®-551 S Elastic Primer | >18 | Sikagard®-675 W GB ElastoColor |
Sikagard®-705 L | >5 | Sikagard®-675 W GB ElastoColor |
Sikagard®-675 W GB ElastoColor | >1 | Sikagard®-675 W GB ElastoColor |
Note:
A refresher coat of Sikagard®-675 GB W ElastoColor can be applied without priming if the existing coat has been thoroughly cleaned.
Applied Product Ready for Use
Final drying: ~24 hours at +20 °C
Consumption
Product | Per coat |
Sikagard®-551 S Elastic Primer | ~ 0.10 - 0.15 kg/m2 |
Sikagard®-552 W Aquaprimer | ~ 0.10 - 0.15 kg/m2 |
Sikagard®-705 L | ~ 0.15 kg/m2 |
Sikagard®-675 W ElastoColor | ~ 0.20 - 0.25 kg/m2 |
APPLICATION
- Sikagard®-675 W GB ElastoColor is supplied ready for use.
- If required, apply appropriate primer to substrate (refer to System Structure).
- Sikagard®-675 W GB ElastoColor can be applied by brush, roller or airless spray.
- For airless spray application: Pressure: ~150 bar. Nozzle bore: 0.38–0.53 mm. Spray angle: ~50–80°.
CLEANING OF TOOLS
Clean all tools and application equipment with water immediately after use. Hardened / cured material can only be removed mechanically.For Sikagard®-551 S Elastic Primer, use Sika® Thinner C.