Parex E33 Epoxy Grout
High strength epoxy resin-based grout
Parex E33 Epoxy Grout is part of the Parex E Epoxy grout range cover a wide range apllications and void thicknesses. Parex E33 Epoxy Grout is a 3 component, high performance, precision, epoxy grouting system. Suitable for placing at temperatures between 5ºC and 45ºC.
- High early strength and fast curing
- Also applicable at low temperatures (in conjunction with Parex E33 winter additive)
- Ready-to-mix, pre-batched units
- Non-shrink
- Corrosion and chemically resistant
- Stress and impact resistant
- High compressive strength
- Good creep resistance
Usage
- Machinery base plates.
- Crane rail tracks.
- Bridge Bearings.
- Compressors and pumps.
- Reciprocating machinery.
- High impact loads.
Advantages
- High early strength and fast curing
- Also applicable at low temperatures (in conjunction with Parex E33 winter additive)
- Ready-to-mix, pre-batched units
- Non-shrink
- Corrosion and chemically resistant
- Stress and impact resistant
- High compressive strength
- Good creep resistance
Packaging
Pre-batched unit | 28.5 kg (A + B + C) |
Product Details
Composition
Epoxy resin
Shelf life
24 months
Storage conditions
Stored properly in original, unopened, sealed and undamaged packaging in dry conditions at temperatures between +5 °C and +30 °C. Protect from direct sunlight.
Density
~1950 kg/m3
Compressive strength
1 day | ~63 N/mm2 |
3 days | ~81 N/mm2 |
7 days | ~85 N/mm2 |
Typical grout values @ 20ºC
Tensile strength in flexure
29 N/mm2 @ 7 days
Tensile strength
16 N/mm2 @ 7 days
Application
Layer thickness
Minimum grout depth: 10mm
Maximum grout depth: 50mm
Flowability
Result from 50mm concentric ring test = 200mm
Flow result of 50mm represents nil flow.
Pot Life
~ 30 mins after mixing
Yield
Each pack will yield approximately 14.75 litres of mixed material.
SUBSTRATE QUALITY
Mortar and concrete must be older than 28 days (dependent on minimum strength requirements).
Verify the substrate strength (concrete, natural stone etc.).
The substrate surface (all types) must be clean, dry and free from contaminants such as dirt, oil, grease,
existing surface treatments and coatings etc.
Steel substrates must be de-rusted to a standard equivalent to Sa 2.5.
The substrate must be sound and all loose particles must be removed.
Substrate must be dry or mat damp and free from any standing water, ice etc.
SUBSTRATE PREPARATION
Substrates must be sound, dry, clean and free from laitance, ice, standing water, grease, oils, old surface treatments or coatings and all loose or friable particles must be removed to achieve a laitance and contaminant free, open textured surface.
Surface and base plate contact area must be clean and sound. For best results, the substrate shall be dry. Remove dust, laitance, oils, grease, curing compounds, impregnations, waxes, foreign particles, coatings, and disintegrated materials by mechanical means, i.e. chipping with a chisel, blast cleaning etc.
All anchor pockets or sleeves must be free of water.
MIXING
Mixing of Parex E33 Epoxy Grout should be carried out with full packs only.
Pour all of the resin and hardener into a clean mixing vessel. Mix with a slow speed drill (200-300rpm) and Mortar Stirrer until homogeneous. Slowly add the filler to the mixed resin and hardener. When all the filler has been added, mix for a further two minutes until an even colour is achieved. Try and ensure that air entrainment is kept to a minimum by keeping the mixing head below the surface level of the grout at all times. Larger volumes may be mixed using a forced action mixer such as the Creteangle or the Pennine.
CLEANING OF EQUIPMENT
Sweep excess grout into appropriate containers for disposal before it has hardened.
Dispose of in accordance with applicable local regulations.
Uncured material can be removed with Sika Thinner C. Cured material can only be removed mechanically.