Product Data Sheet Show all documents
Sika® Icosit® KC 330 FK NEW

Sika® Icosit® KC 330 FK NEW

2-component polyurethane adhesive for fixing filler blocks and joining construction materials

Sika® Icosit® KC 330 FK NEW is a two-component, solvent-free, flexible adhesive based on polyurethane for the application in track construction.

  • Easy to mix and apply. 
  • Excellent weathering and ageing resistance.
  • High initial adhesion.
  • Levels out tolerances.
  • Usually no need for temporary fixation.
  • Vibration reducing.
  • Sound absorbing.
Contact Us
Product Data Sheet Show all documents

Usage

Particularly suited for fixing filler blocks to the web of grooved rails for in-street installation of trackwork. Flexible adhesive designed for, as examples, fixing machinery in industry, and for joining various construction materials, particularly metal and concrete (e. g. for fixing stainless steel cladding to the running surface of clarifiers in sewage treatment plants).   

Advantages

  • Easy to mix and apply. 
  • Excellent weathering and ageing resistance.
  • High initial adhesion.
  • Levels out tolerances.
  • Usually no need for temporary fixation.
  • Vibration reducing.
  • Sound absorbing.

Packaging

Part A

9 kg pail

Part B

1 kg tin

Parts A + B

10 kg

Colour

Black

Product Details

Product Information

Shelf Life

12 months from date of production

Storage Conditions

The product must be stored in original, unopened and undamaged sealed packaging in dry conditions at temperatures between +10 °C and +25 °C. Always refer to packaging.

Density

Part A

~1.4 kg/l

(ISO 2811-1)

Part B

~1.2 kg/l

(ISO 2811-1)

Parts A + B

~1.4 kg/l

(ISO 1183-1)

The density of the mixed material (A + B) is determined by calculation.

 
Technical Information

Shore A Hardness

85 ± 5 (after 28 days)

(ISO 868)

Shore hardness assists with material identification and assessing the curing progress on site.

Tensile Strength

~3 N/mm2

(ISO 527)

Tear Strength

~8.5 N/mm²

(ISO 34 B)

Service Temperature

-40 °C minimum / +80 °C maximum

Short term up to +150 °C

Chemical Resistance

Long-term resistant against:

  • Water
  • Most detergents
  • Sea water, alkaline water

   

Short-term resistant against:

  • Mineral oils, diesel fuel

   

Short-term or no resistance against:

  • Organic solvents (ester, ketone, aromates), alcohol and thinners
  • Concentrated lyes and acids

   

Contact Sika® Technical Services for specific information.

Application

Application Information

Mixing Ratio

Part A : Part B = 100 : 11 (parts by weight)

Layer Thickness

minimum 3 mm / maximum 30 mm

Product Temperature

Condition product parts before application preferably at ~+15 °C to ~+25 °C.

Ambient Air Temperature

+5 °C minimum / +35 °C maximum

Relative Air Humidity

70 % maximum

Substrate Temperature

+5 °C minimum / +35 °C maximum

Substrate Moisture Content

Dry

Pot Life

~15 minutes at +20 °C

After this time, the mixture becomes unusable. Higher temperatures will shorten pot life.

Curing Time

Tack-free: ~3 hours (+20 °C)

Trafficable: ~24 hours (+20 °C)

Waiting Time / Overcoating

Minimum

Maximum

Sika® Icosit® KC 330 Primer

1 hour

3 days

 
Consumption

Consumption

~1.4 kg per litre of volume
Application steps

SUBSTRATE QUALITY

Substrate must be sound, free from oil, grease, loose and friable particles.
Slightly damp substrates are acceptable. Standing water must be removed (e.g. by vacuum extraction or oil free compressed air) before pouring Sika® Icosit® KC 330 FK NEW.

SUBSTRATE PREPARATION

To improve adhesion, apply Sika® Icosit® KC 330 Primer as a primer on absorbent substrates (concrete).

MIXING

Sika® Icosit® KC 330 FK NEW  is supplied in pre-weighed composite units consisting of parts A + B.

 

Part A must be stirred thoroughly before being mixed with part B.

The following mixing instructions must be carried out:

  • Use an electric or pneumatic mixer with basket type stirrer (diameter 120–140 mm, speed ~600–800 rpm).
  • Mixing time ~60 to 80 seconds.
  • Ensure material is mixed from the container walls and the base by the stirrer during mixing.

During mixing until approximately 3 minutes afterwards, material remains liquid (pourable) and subsequently turns into a thixotropic, sag-resistant, trowel-applicable consistency.

CLEANING OF TOOLS

Mixing and application tools must be cleaned at regular intervals and immediately after use with Sika® Thinner C. Hardened material can only be removed mechanically.