Product Data Sheet Show all documents

Sikaplan® WP 1100-32 HL2

Sheet waterproofing membrane for basements and Tunnels

Sikaplan® WP 1100-32 HL2 is a flexible, homogeneous sheet waterproofing membrane with a ≤ 0.2 mm thick signal layer, based on premium-quality polyvinylchloride (PVC-P).

  • High resistance to ageing
  • Based on virgin material with consistent quality
  • Without DEHP (DOP) plasticiser
  • With thin signal layer to indicate damages
  • Optimized flexibility, tensile strength and multi-axial elongation
  • Elastic material behaviour
  • High resistance to mechanical influences
  • Flexible in cold temperatures
  • Suitable for contact with acidic soft water and alkaline environments
  • Resistant to root penetration and micro-organisms
  • Optimized workability, thermally weldable
  • Can be installed on damp and wet substrates
  • Temporary UV stability for installation
  • Self-extinguishing in fire
 
Contact Us
Product Data Sheet Show all documents

Usage

Waterproofing of tunnels and basements against water ingress

Advantages

  • High resistance to ageing
  • Based on virgin material with consistent quality
  • Without DEHP (DOP) plasticiser
  • With thin signal layer to indicate damages
  • Optimized flexibility, tensile strength and multi-axial elongation
  • Elastic material behaviour
  • High resistance to mechanical influences
  • Flexible in cold temperatures
  • Suitable for contact with acidic soft water and alkaline environments
  • Resistant to root penetration and micro-organisms
  • Optimized workability, thermally weldable
  • Can be installed on damp and wet substrates
  • Temporary UV stability for installation
  • Self-extinguishing in fire
 

Packaging

Roll size

2.20 m (width) × roll length individual as specified

Colour

Surface

smooth

Colour

signal layer: yellow

bottom layer: dark grey

Product Details

Sustainability / Certifications / Approvals

APPROVALS / STANDARDS

  • 'Polymeric geosynthetic barrier for use in tunnels and underground structures. Fluid barrier.' according to EN 13491, Declaration of Performance Nr. 0207042010003200001003, certified by notified factory production control certification body 1213, certificate of conformity of the factory production control 1213-CPR-028, and provided with the CE marking.
  • Certified acc. TL/TP (ZTV-ING).
  • Environmental safety certificate BBodSchV / M GeokE
 
Product Information

Shelf Life

5 years shelf life from date of production if stored properly in undamaged, unopened, original sealed packaging

Storage Conditions

Rolls must be stored in their original packaging, in a horizontal position and in cool and dry conditions. They must be protected from direct sunlight, rain, snow and ice, etc.
Do not stack pallets of rolls during transport or storage.

Effective Thickness

3.20 (-5 / +10 %) mm incl. signal layer

(EN 1849–2)

Mass per unit area

4.40 (-5 / +10 %) kg/m2

(EN 1849–2)
System information

System Structure

Ancillary Products:

  • Sikaplan® WP Disc
  • Sikaplan® W Felt PP
  • Sikaplan® W Tundrain
  • Sikaplan® WP Protection Sheet
  • Sika Waterbar® WP for forming compartments, waterproofing of concrete joints and fixings
  • Sikaplan® WP Tape
Technical Information

Tensile Strength

17.0 (± 2.0) N/mm2 (machine direction)(ISO 527)
16.0 (± 2.0) N/mm2 (cross direction)

Burst Strength

≥ 80 % (D=1.0 m)

(EN 14151)

Resistance to Impact

Watertight at 1250 mm drop height

(EN 12691)

(500 g falling weight, Method A)

Long Term Compression Strength

Watertight at 7.0 N/mm2 (50h)

(similar to SIA V280/14)

Foldability at Low Temperature

No cracks at -20 °C

(EN 495–5)

Dimensional Change after Heat

< 2.0 % (machine/ cross)

(EN 1107–2)

(+80 °C / 6 h)

Resistance to Oxidation

Change in elongation

≤ 10 %

Change of tensile strength

≤ 10 %

Behaviour after Storage in Warm Water

Change in tensile strength and elongation

≤ 20 %

   

Change of mass

< 10 %

Chemical Resistance

Saturated Limewash Ca(OH)2

Change in tensile strength and elongation

≤ 20 %

  

5-6% Sulfurous Acid

Change in tensile strength and elongation

≤ 20 %

Foldability at -20 °C: No cracks

Microbiological Resistance

Change of tensile strength

≤ 15 %

Change in elongation

≤ 15 %

Resistance to Weathering

Remaining tensile strength and elongation

≥ 75 % (350 MJ/m2)

Reaction to Fire

Class E

(EN 13501-1)(EN ISO 11925-2)

Behaviour after Heat Welding of Overlaps

Shear resistance of welded seam

Break occurs outside of seam  

Peel resistance of welded seam

≥ 6.0 N/mm

Service Temperature

-10 °C / +35 °C max.

Ambient Maximum Temperature of Liquids

+35 °C

Application

Application Information

Ambient Air Temperature

+5 °C min.
Application steps

SUBSTRATE QUALITY

In-situ concrete: Clean, sound and dry, homogeneous, free from oils and grease, dust and loose or friable particles.
Shotcrete: The profile of the shotcrete surface must not exceed a ratio of length to depth of 10:1 and its min. radius must be 20 cm. The shotcrete surface must not contain broken aggregates. Any leaks must be sealed with Sika® waterproof plugging mortar, or drained with a Sika® FlexoDrain system. Where necessary to achieve the desired profile/surface, apply a fine sprayed concrete layer on the shotcrete surface with a min. thickness of 3-5 cm and aggregate diameter not exceeding 8 mm. Steel (girders, reinforcement mesh, anchors, etc.) must also be covered with a minimum of 4 cm fine sprayed concrete. The shotcrete surface must be clean (no loose stones, nails, wires, etc.).
A polypropylene geotextile (≥ 500 g/m2) or a compatible drainage layer must be installed prior to the Sikaplan® WP 1100-32 HL2 membrane application.