Sikafloor®-221 W Conductive

Sikafloor®-221 W Conductive

Epoxy Water-based Electrostatic Conductive Flooring Primer

Sikafloor®-221 W Conductive is a 2-part, epoxy, water-based, electrostatic conductive flooring primer with increased electrical resistance. It is part of the selected Sikafloor® ECF and ECD flooring systems.

  • Water-based
  • Easy to apply
  • High electrostatic conductivity
  • Applied by roller
Contact Us
Product Data Sheet Show all documents

Usage

  • As a conductive primer below Sikafloor® electrostatic conductive floor coatings.
  • Flooring that needs to comply with the requirements of the standard VDE 100-600.

Advantages

  • Water-based
  • Easy to apply
  • High electrostatic conductivity
  • Applied by roller

Packaging

Part A

4,98 kg container

Part B

1,02 kg container

Part A + B

6 kg unipacks

Refer to current price list for packaging variations.

Colour

Part  A - resin

black, liquid

Part B - hardener

white, liquid   

Final colour: black

Product Details

Sustainability / Certifications / Approvals

ENVIRONMENTAL INFORMATION

Conformity with LEED v4 MR credit 4 option 2: Building product disclosure and optimization - Material ingredients.

 

APPROVALS / STANDARDS

  • CE Marking and Declaration of Performance to EN 1504-2 - Surface protection product for concrete - Coating.
  • CE Marking and Declaration of Performance to EN 13813 - Resin screed material for internal use in buildings.
  • Insulation Resistance DIN VDE 0100-600, Sikafloor® MultiDur ES-47 ECF, kiwa, Test report No. P 12174-4-E.
  • Insulation Resistance DIN VDE 0100-600, Sikafloor® MultiDur ES-47 ESD, kiwa, Test report No. P 12174-2-E.
  • Insulation Resistance DIN VDE 0100-600, Sikafloor® MultiDur ES-48 ECF, kiwa, Test report No. P 12174-3-E.
  • Insulation Resistance DIN VDE 0100-600, Sikafloor® MultiDur ES-49 ECF, kiwa, Test report No. P 12174-5-E.
  • Insulation Resistance DIN VDE 0100-600, Sikafloor® MultiDur ES-52 ESD, kiwa, Test report No. P 12174-1-E.
  • Test of floor IEC 61340-4-1, Sikafloor® MultiDur ES-52 ESD, RISE, Test report No. 9P07719 C.
  • IEC 61340-5-1, Sikafloor® MultiDur ES-52 ESD, RISE, Approval No. 230-19-0040.
 
Product Information

Chemical Base

Water-based epoxy

Shelf Life

12 months from date of production.

Storage Conditions

The product must be stored in original, unopened and undamaged packaging in dry conditions at temperatures between +5 °C and +30 °C. Always refer to packaging.

Density

Part A

1,15 kg/l

Part B

1,09 kg/l

Mixed Resin

1,14 kg/l

Values at +23 °C.

Solid content by mass

~40 %

Solid content by volume

~32 %
Technical Information

Electrostatic Behaviour

Typical Average Resistance to Ground:

Rg ≤ 104 Ω*

In Combination with a Sika® Electrostatic Conductive Floor Covering:

Rg ≥ 107 Ω ≤ 109 Ω*

* Readings may vary, depending on ambient conditions (i.e. temperature, humidity, etc.) and measurement equipment.

Application

Application Information

Mixing Ratio

Part A : Part B = 83 : 17 (by weight)

Ambient Air Temperature

+10 °C minimum / +30 °C maximum

Relative Air Humidity

75 % maximum

 

Dew Point

Beware of condensation.
The substrate and uncured applied floor material must be at least +3 °C above dew point to reduce the risk of condensation or blooming on the floor finish.

Substrate Temperature

+10 °C minimum / +30 °C maximum

Substrate Moisture Content

≤ 4 % percentage by weight

The following test methods can be used: Sika®-Tramex Meter, CM-measurement or Oven-dry-method. No rising moisture according to ASTM (Polyethylene-sheet).

Pot Life

Temperatures

Time

+10 °C

~120 minutes

+20 °C

~90 minutes

+30 °C~30 minutes

Curing Time

Before overcoating Sikafloor®-221 W Conductive allow:

Substrate Temperature

Minimum

Maximum

+10 °C

26 hours7 days

+20 °C

17 hours5 days
+30 °C12 hours4 days

Times are approximate and will be affected by changing ambient conditions particularly temperature and relative humidity.

Applied Product Ready for Use

Temperature

Foot Traffic

+10 °C

~26 hours

+20 °C

~13 hours

+30 °C~8 hours

Times are approximate and will be affected by changing ambient conditions particularly temperature and relative humidity.
Consumption

Consumption

~0,08–0,10 kg/m²

This figure is theoretical and does not allow for any additional material due to surface porosity, surface profile, variations in level or wastage, etc.

For detailed information, refer to the System Data Sheets.
Application steps

MIXING

Prior to mixing all parts, mix separately Part A (resin) using an electric single paddle mixer (300–400 rpm) or other similar equipment. Mix liquid and all the coloured pigment until a uniform colour / mix has been achieved. Add Part B (hardener) to Part A and mix Part A + B continuously for at least 2 minutes until a uniformly coloured mix has been achieved. To ensure thorough mixing, pour materials into a clean container and mix again for at least 1 minute to achieve a smooth, consistent, homogeneous mix. Excessive mixing must be avoided to minimise air entrainment. During the final mixing stage, scrape down the sides and bottom of the mixing container with a straight edge trowel or spatula at least once to ensure complete mixing. Mix full units only. Mixing time for A+B = >3 minutes.

 

APPLICATION

Apply Sikafloor®-221 W Conductive onto the prepared, primed substrate and apply by short pile nylon roller (12 mm), then back roller in two directions at right angles to each other. Ensure a continuous, pore-free coat covers the substrate.

Confirm waiting / overcoating time has been achieved before applying subsequent products.

CLEANING OF TOOLS

Clean all tools and application equipment with water immediately after use. Hardened material can only be removed mechanically.