Sikafloor® MultiDur ES-24 ECF
Sikafloor® ES24 ECF is a, decorative and protective dissipative self-smoothing flooring system for concrete or cement screeds with normal up to medium heavy wear.
- Electrostatic conductive
- Good chemical and mechanical resistance
- Easy to clean
- Economical
- Liquid proof
- Semi-gloss finish
- Slip resistant surface possible
System Structure
1
Conductive primer
2
Conductive final coating
Usage
It is used as:- Decorative and protective electrostatic conductive self-smoothing system for concrete or cement screeds with normal up to medium heavy wear.
- Suitable as a wearing course in industries, such as automotive, electronics and pharmaceutical manufacturing, storage facilities and warehouses.
- Particularly suitable for areas with sensitive electronic equipment e.g. CNC machinery, computer rooms, aircraft maintenance sheds, battery-charging rooms and areas subjected to high explosion risks etc.
Advantages
- Electrostatic conductive
- Good chemical and mechanical resistance
- Easy to clean
- Economical
- Liquid proof
- Semi-gloss finish
- Slip resistant surface possible
Packaging
Please refer to individual Product Data Sheet.
Colour
Almost unlimited choice of colour shades.
Due to the nature of carbon fibres providing the conductivity, it is not possible to achieve exact colour matching. With very bright colours (such as yellow and orange), this effect is increased. Under direct sunlight there may be some variations and colour variation, this has no influence on the function and performance of the coating.
Appearance
Self-smoothing system – gloss finish
System Details
APPROVALS / STANDARDS
- Self-smoothing, coloured epoxy resin coating according to EN 1504-2: 2004 and EN 13813, DoP 02 08 01 02 014 0 000007 2017, certified by Factory Production Control Body No. 0921, certificate 2017, and provided with the CE-mark
- Fire classification in accordance with EN 13501-1, Report-No. 2007-B-0181/17, MPA Dresden, Germany, May 2007
- Testing of Paint Compatibility in acc. to BMW- Standard 09-09-132-5, Polymer Institute, Test Report P 5541, August 2008
- Varnishability test according to VW-standard PV 3.10.7 (paint wetting impairment substances (PWIS)) like silicones, HQM GmbH, Test Report 09-09-132-4, 09.2009
- Particle emission certificate Sikafloor®-262 AS N CSM Statement of Qualification - ISO 14644-1, class 4 - Report No. SI 1412-740, March 2015
- Outgassing emission certificate Sikafloor®-262 AS N F CR: CSM Statement of Qualification - ISO 14644-8, class -8.0 - Report No. SI 1412-740, March 2015
- Spark resistance in accordance with UFGS-09 97 23 of coating systems, Test report P 8625-E, Kiwa Polymer Institut, March 2014
System Structure
Sikafloor® MultiDur ES-24 ECF:
1. Primer + Earthing connection | Sikafloor®-150/-151+ Sika® Earthing Kit |
2. Conductive primer | Sikafloor® - 220 W Conductive |
3. Conductive final coating | Sikafloor® - 262 AS N filled with Sikafloor® Filler 1 |
Note: alternatively quartz sand F34* can be used as a filler, which will result in a gloss finish with a slight change of the aesthetical appearance.
The system configuration as described must be fully complied with and may not be changed.
Composition
Epoxy
Nominal Thickness
~ 1.0 - 1.5 mm
Volatile organic compound (VOC) content
Very low content of volatile organic compounds. Sikafloor®-262 AS N, the finishing layer of the Sikafloor® MultiDur ES-24 ECF System, has been awarded the Frauenhofer IPA CSM Certicate of Qualification with the report number SI 1412-740. The Outgassin test was performed in accordance with CSM procedures. TVOC: ISO-AMC Class -8.0 (see ISO 14644-8). It fulfils the stringent demands for indoor air quality and low VOC emitting products AgBB see the test report no. 392-2014-00286901A.
Shelf Life
Please refer to individual Product Data Sheet.
Storage Conditions
Please refer to individual Product Data Sheet.
Shore D Hardness
~ 77 (resin filled) | (3 days / +23 °C) |
Abrasion Resistance
~ 100 mg (resin filled) | (CS 10/1000/1000) (7 days / +23 °C) |
Compressive Strength
~ 80 N/mm² (resin filled) | (28 days / +23 °C) |
Tensile Strength
~ 40 N/mm² (resin filled) | (28 days / +23 °C) |
Reaction to Fire
Bfl s1 | (EN 13501-1) |
Chemical Resistance
Resistant to many chemicals. Contact Sika technical service for specific information.
Thermal Resistance
Exposure* | Dry heat |
Permanent | +50 °C |
Short-term max. 7 d | +80 °C |
Short-term moist/wet heat* up to +80 °C where exposure is only occasional (i.e. during steam cleaning etc.)
*No simultaneous chemical and mechanical exposure.
USGBC LEED Rating
Conforms to the requirements of LEED EQ Credit 4.2: Low-Emitting Materials: Paints & Coatings SCAQMD Method 304-91 VOC Content < 100 g/l
Electrostatic Behaviour
Resistance to ground1 | Rg < 109 Ω | (IEC 61340-4-1) |
Typical average resistance to ground2 | Rg < 106 Ω | (DIN EN 1081) |
1 In accordance with IEC 61340-5-1 and ANSI/ESD S20.20.
2 Readings may vary, depending on ambient conditions (i.e. temperature, humidity) and measurement equipment.
Application
Ambient Air Temperature
+10 °C min. / +30 °C max.
Relative Air Humidity
80 % r.h. max.
Dew Point
Beware of condensation!
The substrate and uncured floor must be at least 3 °C above dew point to
reduce the risk of condensation or blooming on the floor finish.
Substrate Temperature
+10 °C min. / +30 °C max.
Substrate Moisture Content
<4 % pbw moisture content.
Test method: Sika Tramex Meter, CM-measurement or Oven-Dry-Method.
No rising moisture according to ASTM (Polyethylene-sheet).
Waiting Time / Overcoating
Before applying Sikafloor®-220 W Conductive on Sikafloor®-150/151 allow:
Substrate temperature | Minimum | Maximum |
+10°C | 24 hours | 4 days |
+20°C | 12 hours | 2 days |
+30°C | 8 hours | 1 days |
Before applying Sikafloor®-262 AS N on Sikafloor®-220 W Conductive allow:
Substrate temperature | Minimum | Maximum |
+10°C | 26 hours | 7 days |
+20°C | 17 hours | 5 days |
+30°C | 12 hours | 4 days |
Times are approximate and will be affected by changing ambient conditions particularly temperature and relative humidity.
Applied Product Ready for Use
Temperature | Foot traffic | Light traffic | Full cure |
+10°C | ~ 30 hours | ~ 5 days | ~ 10 days |
+20°C | ~ 24 hours | ~ 3 days | ~ 7 days |
+30°C | ~ 16 hours | ~ 2 days | ~ 5 days |
Note: Times are approximate and will be affected by changing ambient conditions
Consumption
Sikafloor® MultiDur ES-24 ECF System
Coating | Product | Consumption |
Primer | Sikafloor®-150/-151 | 1-2 x ~ 0.3 - 0.5 kg/m² |
Levelling (if required) | Sikafloor®-150/-151 levelling mortar | Refer to PDS of Sikafloor®-150/-151 |
Earthing Connection | Sika® Earthing Kit | 1 earthing point per approx. 200 -300 m², min. 2 per room. |
Conductive Primer | Sikafloor®-220 W Conductive | 1 x 0.08 - 0.10 kg/m² |
Self smoothing wearing course for high aesthetical demands film thickness ~1.5 mm | Sikafloor®-262 AS N filled with Sikafloor® Filler 1* | Maximum 1.6 kg/m² Binder + Sikafloor® Filler 1. Filling grade: 0.1 pbw to 1 : 0.2 pbw (Depending on the air temperature the filling grade varies) |
Self smoothing wearing course film thickness ~1.5 mm | Sikafloor®-262 AS N filled with quartz sand F34* | Maximum 2.5 kg/m² Binder + quartz sand F 34: 1 : 0.1 pbw to 1 : 0.3 pbw (Depending on the air temperature the filling grade varies) |
These figures are theoretical and do not allow for any additional material due to surface porosity, surface profile, variations in level or wastage etc.
* All values have been determined using quartz sand F 34 (0.1-0.3 mm) from Quarzwerke GmbH Frechen and Sikafloor-Filler 1. Other quartz sand type will have an effect on the product, such as filling grade, levelling properties and aesthetics. Generally, the lower the temperature the less the filling grade.