Sikafloor® MultiFlex PB-32 UV
Polyurethane slip and UV-resistant tough-elastic flooring system
Sikafloor® MultiFlex PB-32 UV is a polyurethane, slip and UV-resistant, tough-elastic flooring system. It provides a safe slip resistant surface in dry and wet conditions.
- Thickness ~3.0 mm.
- Good UV resistance
- Good mechanical resistance
- Good chemical resistance
- Scratch resistant surface
- Low dirt pick up
- Easy cleanability
- Seamless
- Slip and skid resistant surface
- i-Cure based technology wearing layer
- Low VOC content
- Low maintenance
- Application on asphalt surfaces
System Structure
Usage
Industrial slip resistant resin flooring on cementitious substrates for:- Life Science production areas
- Automotive production plants
- Storage areas
- Logistic areas
- Multi-storey and underground car park decks and ramps
Advantages
- Thickness ~3.0 mm.
- Good UV resistance
- Good mechanical resistance
- Good chemical resistance
- Scratch resistant surface
- Low dirt pick up
- Easy cleanability
- Seamless
- Slip and skid resistant surface
- i-Cure based technology wearing layer
- Low VOC content
- Low maintenance
- Application on asphalt surfaces
Packaging
Refer to the individual Product Data Sheets
Colour
Seal /Top coat available in many colours. Refer to the Sikafloor®-359 Product Data Sheet
Appearance
Slip resistant, matt finish
System Details
APPROVALS / STANDARDS
- CE Marking and Declaration of Performance to EN 1504-2 - Surface protection product for concrete - Coating
- CE Marking and Declaration of Performance to EN 13813 - Resin screed material for internal use in buildings
- Fire testing EN 13501-1, Sikafloor®-3240, MPA Dresden, Report No. 20150909/01
System Structure
Sikafloor® MultiFlex PB-32 UV (~3.0 mm)
| Layer | Product | Consumption |
| 1. Primer | Sikafloor®-150/-151 | ~0.4 kg/m2/layer |
| 2. Base coat | Sikafloor®-3240 (filled 1:0.5 with quartz sand 0.06–0.3 mm) by weight | ~1.8–2.0 kg/m2 |
| Broadcast | Quartz Sand (0.3–0.8 mm) to excess | ~4.0–5.0 kg/m² |
| 3. Seal / Top Coat | Sikafloor®-359 N | ~0.7–0.9 kg/m2 |
On substrates with hot poured/mastic asphalt, use Sikafloor®-3240 as a primer .
These figures are theoretical and do not allow for any additional material due to surface porosity, surface profile, variations in level or wastage etc.
Composition
Polyurethane
Nominal Thickness
~3 mm
Shelf Life
Refer to the individual Product Data Sheets
Storage Conditions
Refer to the individual Product Data Sheets
Shore D Hardness
~60 (7 days / 23 °C / 50 % r.h.) | (DIN 53505) |
Abrasion Resistance
~160 mg (CS 10/1000/1000) | (DIN 53109) |
Tensile Strength
~14 N/mm2 (14 days / 23 °C / 50 % r.h.) | (DIN EN ISO 527-2) |
Tensile Adhesion Strength
| > 2.0 N/mm2 | (EN 13892-8) |
Reaction to Fire
Bfl-s1 | (EN 13501-1) |
Chemical Resistance
Sikafloor® MultiFlex PB-32 UV always has to be sealed with Sikafloor®-359. Refer to the chemical resistance of Sikafloor®-359.
Skid / Slip Resistance
R10 / R11 | (DIN 51130) |
Application
Product Temperature
+10 °C min. / +30 °C max.
Ambient Air Temperature
+10 °C min. / +30 °C max.
Relative Air Humidity
80 % max.
Dew Point
Beware of condensation.
The substrate and uncured applied floor material must be at least +3 °C above dew point to reduce the risk of condensation or blooming on the surface of the applied product.
Substrate Temperature
+10 °C min. / +30 °C max.
Substrate Moisture Content
≤4 % parts by weight
The following test methods can be used: Sika®-Tramex meter, CM - measurement or Oven-dry-method. No rising moisture according to ASTM (Polyethylene-sheet).
Applied Product Ready for Use
| Temperature | Foot traffic | Light traffic | Full cure |
| +15 °C | ~72 hours | ~6 days | ~10 days |
| +20 °C | ~24 hours | ~4 days | ~7 days |
| +30 °C | ~18 hours | ~2 days | ~5 days |
Times are approximate and will be affected by changing ambient conditions particularly temperature and relative humidity.
CLEANING
Refer to Sika Information Manual: Sikafloor®-Cleaning Regime