Sikafloor®-2350 ESD

• Conformity with LEED v4 MRc 2 (Option 1): Building Product Disclosure and Optimization — Environmental Product Declarations
• Conformity with LEED v4 MRc 4 (Option 2): Building Product Disclosure and Optimization — Material Ingredients
• Conformity with LEED v4 EQc 2: Low-Emitting Materials
• IBU Environmental Product Declaration (EPD) available
• VOC emission certificate according to AgBB und DIBt approval requirements
• Class A+ according to French Regulation on VOC emissions 

• CE Marking and Declaration of Performance to EN 13813:2002 — Screed ma-terial and floor screeds — Synthetic resin screed material
• CE Marking and Declaration of Performance to EN 1504-2:2004 — Products and systems for the repair and protection of concrete structures — Part 2: Sur-face protection systems for concrete — Coating
• Fire classification report, EN 13238, Ghent University, Report No. 20-1069-02
• Slip resistance DIN 51130, Sikafloor®-2350 ESD, Roxeler, Certificate No. 020243-20-3; 020243-20-3a
• Slip resistance DIN 51130, Sikafloor®-2350 ESD, Roxeler, Certificate No. 020243-20-2; 020243-20-2a 

Epoxy

12 months from date of production

The product must be stored in original, unopened and undamaged sealed packaging in dry conditions at temperatures between +5 °C and +30 °C. Always refer to packaging.

Refer to current Safety Data Sheet for information on safe handling and storage.

100 %

100 %

Note: Measurement results can be affected by ESD clothing, ambient conditions, measurement equipment, cleanliness of the floor and the test personnel.

IMPORTANT:

No simultaneous mechanical and chemical strain

While the product is exposed to temperatures up to +60 °C, do not also subject it to chemical and/or mechanical strain, as it may cause damage to the product.

80 % r.h. max.

Beware of condensation. The substrate and uncured applied product must be at least +3 °C above dew point to reduce the risk of condensation or blooming on the surface of the applied product. Low temperatures and high humidity conditions increase the probability of blooming.

< 4 % parts by weight (Sika® Tramex moisture meter)

No rising moisture (ASTM D4263, polyethylene sheet)

The substrate must be visibly dry with no standing water.

Note:Times are approximate and will be affected by changing ambient conditions, particularly temperature and relative humidity.

Note: These figures are theoretical and do not allow for any additional material due to surface porosity, surface profile, variations in level, wastage or any other variations. Apply product to a test area to calculate the exact consumption for the specific substrate conditions and proposed application equipment.

IMPORTANT:

Strictly follow installation procedures

Strictly follow installation procedures as defined in Method Statements, application manuals and working instructions which must always be adjusted to the actual site conditions.

APPLICATION EQUIPMENT

Refer to individual application text.

MIXING EQUIPMENT

Electric double paddle mixer (> 700 W, 300 to 400 rpm)

For self-smoothing wearing layer

1. Mix Part A (resin) for ~10 seconds with a single paddle mixer (300–400 rpm).
2. Add Part B (hardener) to Part A.
3. Switch to an electric double paddle mixer (300–400 rpm, > 700 W).
4. While mixing Parts A + B, gradually add the required filler or aggregates.
5. (Optional) If necessary, gradually add the required amount of Sika® Extender T (refer to Consumption).
6. Mix for a further 2 minutes until a uniform mix is achieved.
7. To ensure thorough mixing, pour materials into another container and mix again to achieve a smooth and uniform mix.
8. During the final mixing stage, scrape down the sides and bottom of the mix-ing container with a flat or straight edge trowel at least once to ensure com-plete mixing.

IMPORTANT:

Temporary heating

If temporary heating is required, do not use gas, oil, paraffin or other fossil fuel heaters. These produce large quantities of both carbon dioxide and water vapour, which may adversely affect the finish. For heating, use only electric powered warm air blower systems.

IMPORTANT:

Performing pre-trials

Pre-trials/mock-up applications must be performed and procedures agreed with all parties before full project application.

IMPORTANT:

Temporary moisture barrier

Before application, confirm substrate moisture content, relative air humidity, dew point, substrate, air and product temperatures. If moisture content is > 4 % parts by weight, Sika®floor® EpoCem® may be applied as a Temporary Moisture Barrier (T.M.B.) system.

SMOOTH WEARING LAYER

Suitable application equipment

Large-Surface Scraper No. 656, Toothed blades No. 25 (www.polyplan.com)

Procedure

1. Pour the mixed Product onto the substrate.
   Note:The consumption is specified in Application Information.
2. Apply the Product evenly over the surface with a serrated trowel.
3. To achieve a smooth finish, smooth the surface with the flat side of a trowel.
4. Back roll the surface in two directions at right angles with a steel spike roller.

TEXTURED WEARING LAYER

Suitable application equipment

• Trowel No. 999 (www.polyplan.com)
• Adhesive Spreader No. 777, Toothed blades No. 23 = A3 (www.polyplan.com)

Procedure

1. Pour the mixed Product onto the substrate.
   Note:The consumption is specified in Application Information.
2. Apply the Product evenly over the surface with a serrated trowel.
3. Back roll the surface in two directions at right angles with a textured roller.

Clean all tools and application equipment with Sika® Thinner C immediately af-ter use. Hardened material can only be removed mechanically.