Sikagard®-406 W
Sikagard®-406 W is a single component white, waterborne acrylic resin based surface coating containing an organic in film preservative with a mat finish.
- Easy to apply
- Good resistance to repeated cleaning regimes using mild detergents and cleaning solutions
- Tough and highly durable
- Good covering and hiding power (opacity)
- Permeable to water vapour
- Ultra-low emission
- More flexible in comparison to standard paints, improved resistance to cracking and flaking
- Mat finish
- Seamless, easy to clean finish
- Low odour
Usage
- Top coat or standalone coating for internal walls and ceilings
- For concrete, bricks, cement based and gypsum substrates, metallic surfaces, timber, tiles and plastic
- Suitable for pharmaceutical, medical engineering, food and beverage industry, hospitals, healthcare facilities, kitchens and prisons and leisure facilities
Advantages
- Easy to apply
- Good resistance to repeated cleaning regimes using mild detergents and cleaning solutions
- Tough and highly durable
- Good covering and hiding power (opacity)
- Permeable to water vapour
- Ultra-low emission
- More flexible in comparison to standard paints, improved resistance to cracking and flaking
- Mat finish
- Seamless, easy to clean finish
- Low odour
Packaging
5.0 l (= 6.60kg) drums
15.0 l (= 19.80 kg) containers
Colour
Available colours BS08B15, BS12B21, BS14C31, BS18E49, BS18E50, RAL1013, RAL3015, RAL7035, RAL9001, White
Product Details
ENVIRONMENTAL INFORMATION
LEED Rating
Sikagard®-406 W conforms to the requirements of LEED EQ Credit 4.2: Low –Emitting Materials: Paints & Coatings SCAQMD Method 304-91 VOC Content < 100 g/l
APPROVALS / STANDARDS
- Exova Warrington fire, test report No. 363981 & 363982, behaviour to fire according to BS 476, April 27, 2016
- Eurofins, test report No. 392-2015-00386902, determination of VOC and SVOC content according to ISO 11890-2/ ASTM D6886, December 10, 2015
- PRA, test report No. 77564-049, gloss, fineness, grind wet scrub resistance and contrast ratio according to EN 13300, November 21, 2015.
- IMSL, test report 2015/02/004.1A, determination of antibacterial activity according to ISO 22196, May 12, 2015
- Campden BRI Group, test report No. S/REP/138532/2, Sensory Evaluation of the Taint Potential, Triangle Test Method TES-S-002 according to EN ISO 4120:2007, Odour Transfer Method, February 8, 2016
- TÜV Rheinland, test report 21246824001, determination of VOC emission according to French Regulations Decret DEVL 1101903D and Decret DEVL 11034675A, November 18, 2015
- 4wardtesting, test report No. C 2906, water vapour permeability according to ISO 7783-1:2000, January 5, 2016
Chemical Base
Waterborne acrylic copolymer dispersion
Shelf Life
12 month from date of production
Storage Conditions
From date of production if stored properly in closed, sealed undamaged packaging in dry conditions at temperatures between +5°C and +30°C. Protect from direct sunlight and frost.
Density
~1.24 kg/l | (DIN EN ISO 2811-1) |
Solid content by weight
~52 %
Solid content by volume
~40 %
Tensile Strength
~10 N/mm² unreinforced | (EN ISO 527-3) |
Tensile adhesion strength
> 1.5N/mm² | to concrete using Sika Bonding Primer |
Chemical Resistance
Good short-term resistance to weak acids, alkalis and cleaning products. Please contact Sika technical service for specific information.
Disinfection with Hydrogen Peroxide Vapour:
- Resistant when using Steris VHP technology
- Resistant to PEA vaporisation technology, when a system build up with glass fibre reinforcement is used
- Resistant when using Oxypharm vaporiser type Nocospray under following conditions:
Disinfectant | Concentration | Setting at vaporiser | Contact time |
NOCOLYSE Mint (6 %) | 1 ml/m³ | 20 m³ (1.5 minutes vaporisation) | 30 min |
NOCOLYSE One Shot (12 %) | 3 ml/m³ (2 cycles) | 45m³ (5 minutes vaporisation) | 30 min |
NOCOLYSE Food (7.9 %) | 1 ml/m³ | 20 m³ (1.5 minutes vaporisation) | 30 min |
NOCOLYSE Food (7.9 %) | 5 ml/m³ (2 cycles) | 75m³ (5 minutes vaporisation) | 60 min |
Application
Ambient Air Temperature
+8°C min. / +35°C max.
Relative Air Humidity
< 80%
Dew Point
Beware of condensation!
The substrate must be at least 3 °C above dew point to reduce the risk of condensation or blooming on the wall finish.
Substrate Temperature
+8 °C min. / +35 °C max.
Substrate Moisture Content
Visible damp free, < 6 % pbw moisture content test method: Sika®-Tramex meter
Curing Time
Before applying Sikagard®-406 W to Sikagard®-406 W allow:
Substrate temperature | Minimum | Maximum |
+10 °C | 4 hours | 7 days |
+20 °C | 2 hours | 7 days |
+30 °C | 1 hour | 7 days |
Before applying Sikagard®-406 W to Sikagard®-403 W allow:
Substrate temperature | Minimum | Maximum |
+10 °C | 4 hours | 7 days |
+20 °C | 1 hour | 7 days |
+30 °C | 1 hour | 7 days |
Applied Product Ready for Use
Temperature | Tack free | Full cure |
+10 °C/ 50 % r.h. | ~ 8 hours | ~ 7days |
+20 °C/ 50 % r.h. | ~ 4 hours | ~ 7days |
+30 °C/ 50 % r.h. | ~ 3 hours | ~ 7days |
Consumption
~0.23kg/m² per layer
~0.18 l/m² per layer
APPLICATION
Stir product until a uniform liquid is achieved. Use low speed stirrer (300-400 rpm) to avoid air entrapment.
For Roller application use short piled roller.
For airless application use tip size from 0.38 to 0.53mm and angle from 40° to 60°.
CLEANING OF TOOLS
Clean all tools and application tolls with water immediately after use. Hardened and/ or cured material can only be removed mechanically or with proprietary paint stripper.