Sika Poxicolor® Primer HE NEW
2-pack primer coat based on epoxy resin. Economically and high-performance corrosion protection also for manually de-rusted surfaces and surfaces prepared by high-pressure water jetting. Low solvent content according to Protective Coatings Directive of German Paint Industry Association (VdL-RL 04).
- Surface tolerant
- High layer thickness and diffusion resistance combined with very good surface wetting properties and adhesion result in a very high safety margin for good corrosion protection
- Fast initial drying and full hardening
- High-build application
- Very economically due to high coverage
Usage
To be used in the Sika Pro-Tecta Cut-Edge Corrosion System. Tough hard, versatile overcoatable primer for corrosion protection on steel exposed to atmosphere. Especially suitable for use on surfaces where only manually de-rusting (wirebrushing or power tool cleaning) or high-pressure water jetting is feasible or economic.Advantages
- Surface tolerant
- High layer thickness and diffusion resistance combined with very good surface wetting properties and adhesion result in a very high safety margin for good corrosion protection
- Fast initial drying and full hardening
- High-build application
- Very economically due to high coverage
Packaging
| Sika Poxicolor® Primer HE NEW | 28kg, 14kg and 4kg net |
| Sika® Thinner EG | 25 Litres, 10 Litres and 3 Litres |
| SikaCor® Cleaner | 160 Litres and 25 Litres |
Colour
Aluminium, sand-yellow and red-brown (mat.-no.: 694.01/02/06)
Product Details
APPROVALS / STANDARDS
- Approved according to German standard ‘TL/TP-KOR-Stahlbauten, page 94'.
Shelf Life
2 years
Storage Conditions
In originally sealed containers in a cool and dry environment
Density
| Sika Poxicolor® Primer HE NEW aluminium |
|
| Sika Poxicolor® Primer HE NEW red-brown, sand-yellow |
|
Solid Content
| Sika Poxicolor® Primer HE NEW auminium | ~67% by volume ~80% by weight |
| Sika Poxicolor® Primer HE NEW red-brown, sand-yellow | ~68% by volume ~83% by weight |
Chemical Resistance
Weathering, de-icing salts, oils and grease and short term exposure to fuels and solvents
Thermal Resistance
Dry heat up to + 100°C
Damp heat up to + 40°C
Application
Mixing Ratio
Components A : B |
| By weight | 88 : 12 |
Thinner
Sika® Thinner EG
If necessary max. 5% Sika® Thinner EG may be added to adapt the viscosity.
Product Temperature
Min. + 5°C
Relative Air Humidity
Max. 85 %, except the surface temperature is significantly higher than the dew point temperature, it shall be at least 3 K above dew point.
Surface temperature
Min. + 5°C
Pot Life
| At + 5°C | ~6 hours |
| At + 20°C | ~4 hours |
Drying stage 6
| Dry film thickness 100 microns | |
| + 5°C after | 12 hours |
| + 20°C after | 6 hours |
| + 30°C after | 3 hours |
Waiting Time / Overcoating
Min.: until drying stage 6 is achieved
Max.: 1 year
Drying time
Final drying time
Depending on layer thickness and temperature final hardness is achieved within 1 - 2 weeks
Consumption
Theoretical material-consumption/VOC without loss for medium dry film thickness:
| Sika Poxicolor® Primer HE NEW aluminium | Sika Poxicolor® Primer HE NEW red-brown, sand-yellow | |
| Dry film thickness | 100 microns | 100 microns |
| Wet film thickness | 150 microns | 150 microns |
| Consumption | ~0.190 kg/m2 | ~0.210 kg/m2 |
| VOC | ~39 g/m2 | ~35 g/m2 |
SURFACE PREPARATION
Steel:
Surface in accordance with ISO 12944-4 Sa 2 ½.
The required degree depends on future exposure.
In case of atmospherically exposure St 2 or St 3 is sufficient.
Note: Sika Poxicolor® Primer HE NEW is not recommended for continuous immersion. In addition, the surface must be dry, free of dirt, oil, grease and loose rust.
Hot dip galvanized surfaces:
Free from oil, grease and zinc salts.
In case of permanent condensation surfaces should be sweep blasted according to ISO 12944-4.
Contaminated surfaces e.g. galvanized surfaces, primed areas or old coatings we recommend to clean with SikaCor® Wash.
MIXING
Stir component A very thoroughly using an electric mixer (start slowly, then increase up to approx. 300 rpm). Add component B carefully and mix both components very thoroughly (including sides and bottom of the container). Mix for at least 3 minutes until a homogeneous mixture is achieved. Fill mixed material into clean container and mix again shortly as described above. During mixing and handling of the materials always wear protective goggles, suitable gloves and other protective clothings.
APPLICATION
The method of application has a major effect on achieving uniform thickness and appearance. Spray application will give the best results. The indicated dry film thickness is easily achieved by airless spray. Adding solvents reduces the sag resistance and the dry film thickness. In case of application by roller or brush, additional applications may become necessary to achieve the required coating thickness, depending on type of construction, site conditions, colour shade etc. Prior to major coating operations a test application on site may be useful to ensure the selected application method will provide the requested results.
By brush:
- Surface preparation St 2 or St 3
- With brush application best penetration and surface wetting is achieved
Conventional high pressure spraying:
- Nozzle size 1.7 - 2.5mm
- Pressure 3 - 5 bar
Airless-spraying:
- Pressure of min. 180 bar
- Diameter of hoses min. 10mm (⅜ inch)
- Nozzle size 0.38 - 0.53mm (0.015 - 0.021 inch)
- Spraying angle 40°- 80°
CLEANING OF TOOLS
SikaCor® Cleaner