Sikafloor® Level-30
High performance, self levelling and fast drying, cementitious screed for interior or exterior in 4 – 30 mm
Sikafloor® Level-30 is a polymer modified, pumpable, self levelling fast drying cementitious screed for higher thickness interior or exterior floors, meeting the requirements of class R3 according to EN 1504-3.
- Self smoothing and highly fluid
- Easy to place by pump or manual application
- Ready for use.
- Low shrinkage.
- Maintains good workability and joint healing throughout its pot life
- Fast setting and drying
- 3-4 hours walk on time (+20 °C)
- Good surface appearance and hardness
- Excellent freeze-thaw salt resistance. (R3)
- Casein and Formaldehyde free
- Suitable for use with under floor heating systems
Usage
Sikafloor® Level-30 is an floor self levelling screed to level or smooth screeds and concrete floors at a thickness between 4–30mm in one working step.Sikafloor® Level-30 is useable as screed for industrial service conditions when sealed with a PU or EP resin top coat from medium to high load (heavy-traffic + forklift pallet truck with impact load )
Sikafloor® Level-30 is also suitable for filling, smoothing and levelling of suitable substrates before applying parquet, ceramic tiles, seamless resinfloors, textile, elastic floor coverings
Sikafloor® Level-30 is useable as screed for exterior areas when sealed with a covering e.g. a coating.
- Suitable for restoration work (Principle 3, method 3.1 of EN 1504-9).
- Suitable for structural strengthening (principle 4,method 4.4 of EN 1504-9).
- Suitable for preserving or restoring passivity (Principle7, method 7.1 and 7.2 of EN 1504-9).
Advantages
- Self smoothing and highly fluid
- Easy to place by pump or manual application
- Ready for use.
- Low shrinkage.
- Maintains good workability and joint healing throughout its pot life
- Fast setting and drying
- 3-4 hours walk on time (+20 °C)
- Good surface appearance and hardness
- Excellent freeze-thaw salt resistance. (R3)
- Casein and Formaldehyde free
- Suitable for use with under floor heating systems
Packaging
25 kg bags
Colour
Powder - beige-grey
Product Details
ENVIRONMENTAL INFORMATION
- EC 1plus R: Very low emissions.
APPROVALS / STANDARDS
- Cement based screed CT-C40-F10-A12 according to EN 13813, declaration of performance 90432755, and provided with CE marking
- Cement based screed A1/A1fl according to EN 13813, declaration of performance 90432755, assessed by notified laboratory 1140, and provided with CE marking
- Cement based screed class R3 for the principles 3 (CR), 4 (SS) and 7 (RP) according to EN 1504-3, declaration of performance 36581792, assessed by notified laboratory 1139, and provided with CE marking
Chemical Base
Polymer modified rapid hardening cement.
Shelf Life
9 months from date of production
Storage Conditions
stored properly in original, unopened and undamaged packaging in dry conditions at temperatures between +5 °C and +30 °C.
Density
~ 2.0 kg/l
Bulk Density
~ 1.25 kg/l
System Structure
| Priming | See substrate pre-treatment |
| Levelling | Apply to the required thickness 4–30 mm |
| Sealer | Sikafloor®-304W, -305W and -2540W |
| Coatings | All kinds Sikafloor® EP and PU coatings |
| Adhesives | Sikabond® -T52, -T54 , -T54FC |
Abrasion Resistance
|
|
|
|
|
|
|
|
AR 0.5 | < 50 μm | BCA |
|
|
|
|
Compressive Strength
| Time | Temperature | Value |
| 24 hours | 20 °C | ~ 20 N/mm2 |
| 28 days | 20 °C | ≥ 40 N/mm2 |
Flexural Strength
| Time | Temperature | Value |
| 24 hours | 20 °C | ~ 3 N/mm2 |
| 28 days | 20 °C | ≥ 10 N/mm2 |
Tensile adhesion strength
| Time | Temperature | Value |
| 28 days | +20 °C | ≥ 1.5 N/mm2 |
Coefficient of Thermal Expansion
| α ~ 16.3x10-6 / °C (for temperature range -20 °C and +40 °C) | (EN 1770) |
Water Absorption
| W ~ 0.5 kg / (m2 x h0.5 ) | (EN 13057) |
Application
Mixing Ratio
5 to 5.25 L water for 25 kg Sikafloor® Level-30
Layer Thickness
4 - 30 mm
Ambient Air Temperature
≥ +10 °C and ≤ +25 °C
Relative Air Humidity
< 75 %
Substrate Temperature
≥ +10 °C and ≤ +25 °C
Substrate Pre-Treatment
Normal intended use of the floor
The one part acrylic primer Sikafloor®-01 Primer is recommended for a pore free surface with very good surface adhesion. Refer to the relevant PDS for the recommended application details etc.
High loads intended use of the floor
Priming with epoxy resins such as Sikafloor® -155WN, Sikafloor® -150 or Sikafloor® -151 fully broadcast with quartz sand 0.3–0.8 mm.
Pot Life
Temperature and Relative Air Humidity | Time |
+23 °C / 50% | ~ 25 minutes |
The temperature will affect the pot life.
Application at temperatures above +23 °C will reduce the pot life and the working time. Temperatures below +23 °C will increase the pot life and extend the working time.
Waiting Time / Overcoating
| Covering | Layer Thickness | Waiting Time |
| Impermeable or moisture sensitive coatings | ≤ 15 mm | 24 hours1 |
| Impermeable or moisture sensitive coatings | ≤ 30 mm | 48 hours1 |
| Cermanic covering | ≤ 30 mm | 24 hours |
- Times are approximate and at +23 °C and 50% r.h. and thus will be affected by changing substrate and ambient conditions, particularly the temperature and relative humidity.
When overcoating Sikafloor® Level-30 always ensure the moisture content has achieved the required value for the coating product, as the waiting time will vary with the application thickness and ambient humidity. (Refer to the coating product data sheet)
Applied Product Ready for Use
At +20 °C and 50% r.h.
Foot traffic | ~ 3 hours |
Lightly serviceable | ~ 24 hours |
Note: Times are approximate and will be affected by changing substrate and ambient conditions, particularly the temperature and relative humidity.
Consumption
~ 1.8 kg/m2/mm
MIXING
By Hand
For 25 kg Sikafloor® Level-30 is required 5 to 5.25 l water. When mixing manually add the dry powder (25 kg) into a container with the clean water.
Mix thoroughly for a minimum of 3 minutes, by use of an electric stirrer, recommended is the use of a double disc stirring paddle or a spiral mix paddle (< 500 rpm).
maturing time: After mixing leave the material to stand in the container for ~ 2 minutes until the majority of air bubbles have dispersed.
Pumping
When using a mortar pump with appropriate equipment (Putzmeister MP 20/25, DuoMix 2000 or PFT G5 FE) set the machine in a way that a uniform mixture is achieved. The use of a remixer is recommended.
Control the water dosage to achieve the required flow, measuring the final average flow diameter on a flat, clean, dry flow table.
| Tool | Flow | Standard |
| Ø = 30 mm H = 50 mm | 130 mm ± 5 mm | EN 12706 |
| Ø 70 / 100 mm H = 60 mm | 355 mm ± 10 mm | ASTM C 230-90 EN1015-3 |
| Ø = 60 mm H = 120 mm | 290 mm ± 10 mm | Sika AT method |
APPLICATION
Pour the mixed material onto the primed surface and apply by trowel or pin screed rake to the required thickness. Roll thoroughly with a spiked roller in two directions to remove any entrapped air. Best application time would be during falling temperatures.
CLEANING OF TOOLS
Clean all tools and application equipment with water immediately after use. Hardened / cured material can only be removed mechanically.