Sikacrete®-213 F

Sikacrete®-213 F

Wet sprayed fire protection mortar

Sikacrete®-213 F is a one-part, cementitious, fire protection mortar for wet spray or hand application. Suitable for fire protecting all types of reinforced concrete buildings and civil engineering structures including tunnels. It contains phyllosilicate aggregates, which are highly effective in resisting the heat of hydrocarbon fires. The fire protection performance allows a reduced thickness of fire protection required compared to concrete. The fire protection layer thickness depends on the specified fire resistance.

  • Pre-bagged dry mortar mix.
  • Application by the wet spray process or by hand. 
  • Minimal layer thickness to comply with fire regulations.
  • Does not contribute to the formation of smoke or toxic fumes during a fire.
  • Lightweight, low density.
  • Easily surface finished by trowel or wooden float.
  • >240 minutes fire resistance achievable.
  • Minimal rebound.
Contact Us
Product Data Sheet Safety Data Sheet Show all documents

Usage

  • Fire protection of concrete and reinforced concrete structures exposed to fire risk.
  • Fire protection of concrete member reinforced with FRP (e.g. Sika® CarboDur® and SikaWrap®).
  • Factory made lightweight (LW) rendering and plastering mortar intended for interior and exterior use in walls, ceilings, columns and partitions as per EN 998-1. 
 

Advantages

  • Pre-bagged dry mortar mix.
  • Application by the wet spray process or by hand. 
  • Minimal layer thickness to comply with fire regulations.
  • Does not contribute to the formation of smoke or toxic fumes during a fire.
  • Lightweight, low density.
  • Easily surface finished by trowel or wooden float.
  • >240 minutes fire resistance achievable.
  • Minimal rebound.

Packaging

9 kg bag

Refer to current price list for packaging variations

Colour

Grey powder

Product Details

Sustainability / Certifications / Approvals

APPROVALS / STANDARDS

  • 3 hours fire testing to EN 1363-1 (RWS curve), VSH, Report No. 20200010.
  • 4 hours fire testing, Lachenbrand curve, VSH, Report No. 20090011.
  • 4 hours fire resistance testing over SikaWrap® and Sika® CarboDur®, NRC, Reports No. B4247.1 & B4247.2.
  • CE Marking and Declaration of Performance to EN 998-1 —  Factory made lightweight (LW) rendering and plastering mortar intended for interior and exterior use in walls, ceilings, columns and partitions. 
Product Information

Chemical Base

Portland cement, additives and phyllosilicate aggregates

Shelf Life

12 months from date of production if stored properly in undamaged unopened, original sealed packaging

Storage Conditions

The product must be stored in original, unopened and undamaged packaging in dry conditions at temperatures between +5 °C and +30 °C. Always refer to packaging.

Maximum Grain Size

~3 mm

Density

Powder

~0,5 kg/L

Fresh applied

~1,0 kg/L (sprayed)

Applied after 28 days

~0,6 kg/L (sprayed)
System information

System Structure

Bonding Primer

  • Sika MonoTop®-1010.

Reinforcement

Structure

Reinforcement Type

Tunnels*

Galvanised or stainless steel. Wire diameter 1 - 2 mm. Mesh size 50 mm.

Other structures

According to the application thickness.**

* A light mesh is always recommended in order to prevent debonding of the mortar layer.

** Contact Sika Technical Services for more information.

Fire Protection Mortar

  • Sikacrete®-213 F.

Surface Protection

Structure

Exposure

Surface Protection

Tunnels and other structuresInternal and normal exposure.No protection required.
Other structures

Exposure to frost, freeze-thaw cycles, de-icing salt.

Improved resistance to mechanical wear (with pore sealer).

Sikagard®-675 W GB ElastoColor.
Technical Information

Compressive Strength

~1,5 N/mm2

(EN 1015-12)

Tensile adhesion strength

≥ 0,25 MPa

Thermal Conductivity

λ10, dry,mat ≈ 0,14 W/m·K

Thermal conductivity of the material at an average temperature of 10 °C in dry state, table A.12 50 % fractile value

                      (EN 1745)

Water Absorption

Wc0

(EN 1015-18)

Diffusion Resistance to Water Vapour

µ ≤ 6

Freeze Thaw De-Icing Salt Resistance

To be resistant to frost, freeze-thaw cycles and de-icing salts, the surface of the mortar must be treated with Sikagard® Wallcoat T.

Reaction to Fire

Euroclass A1

Application

Application Information

Mixing Ratio

8 – 10 L of water per 9 kg bag

Layer Thickness

Minimum: 10 mm

Maximum: 40 mm (per layer)

Ambient Air Temperature

5 °C min. / 30 °C max.

Substrate Temperature

5 °C min. / 30 °C max.
Consumption

Consumption

~5 – 6 kg/m2/10 mm thickness

This figure is theoretical and does not allow for any additional material due to surface porosity, surface profile, variations in level or wastage, etc.
Application steps

EQUIPMENT

Select the most appropriate equipment required for the project:

Substrate Preparation

  • High pressure water blasting system.

Mixing

  • Large quantities shall be mixed in a suitable forced action mixer. Small quanities can be mixed using a low speed electric single or double paddle mixer (<500 rpm).

Application

  • Wet Spray: All-in-one mixing and spraying machine or separate spraying machine and all associated ancillary equipment to suit application volumes.
  • Hand: Clean containers, plasterer's hawk and trowel.

Finishing

  • Trowel (PVC or wooden).
  • Sponge.

MIXING

Important: The consistency must be checked after every mix.

  1. Pour the minimum recommended clean water quantity into a suitable clean mixing container / equipment.
  2. While stirring slowly, add the powder to the water.
  3. Mix thoroughly for at least for 5 minutes, adding additional water if necessary to the maximum specified amount, adjusting to the required consistency to achieve a smooth consistent mix.

APPLICATION

Strictly follow installation procedures as defined in method statements, application manuals and working instructions which must always be adjusted to the actual site conditions.

Important: Avoid application in direct sun and / or strong winds.

Important: Do not add water over the recommended dosage.

Sprayed Application - Wet Spray

Note: Include light wire mesh as required.

  1. Place the wet mixed Sikacrete®-213 F into the suitable wet spraying equipment and apply onto the pre-wetted substrate between the minimum and maximum layer thicknesses without the formation of voids.
  2. Where layers are to be built up, to prevent sagging or slumping, each layer must be allowed to harden before applying subsequent layers “wet on wet”.

Hand Application

Note: Include light wire mesh as required.

  1. Place workable amounts of the wet mixed Sikacrete®-213 F onto a plasterer's hawk and apply onto the pre-wetted substrate with a trowel between the minimum and maximum layer thicknesses without the formation of voids.
  2. Where layers are to be built up, to prevent sagging or slumping, each layer must be allowed to harden before applying subsequent layers “wet on wet”.

Surface Finishing

Important: Do not add additional water during the surface finishing as this can cause discolouration and cracking.

  • Carry out finishing to the required surface texture using suitable finishing tools up to one hour after application, dependent on the temperature and humidity.

CURING TREATMENT

Important: Curing compounds must not be used when they could adversely affect subsequently applied products and systems.

  • Protect fresh mortar immediately from freezing and premature drying using an appropriate curing method (e.g. curing compound, moist geotextile membrane, polythene sheet, thermal blankets, etc.). 
 

CLEANING OF TOOLS

Clean all tools and application equipment with water immediately after use. Hardened material can only be removed mechanically.